- 熔體流動速率 [g/10min]: 2.2
- 密度 [g/cm3]: 0.919
- 拉伸強度 [MPa]: 10.3
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in3 | ASTM D1505 |
| Melt Flow | 2.2 g/10 min | 2.2 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 11.7 MPa | 1700 psi | ASTM D638 |
| Tensile Strength, Yield | 10.3 MPa | 1500 psi | ASTM D638 |
| Elongation at Break | 600 % | 600 % | ASTM D638 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.27 @Frequency 1e+6 Hz | 2.27 @Frequency 1e+6 Hz | ASTM D1531 |
| Dissipation Factor | 0.000060 @Frequency 2.00e+9 Hz | 0.000060 @Frequency 2.00e+9 Hz | ASTM D1531 |
| 0.000080 @Frequency 1e+6 Hz | 0.000080 @Frequency 1e+6 Hz | ASTM D1531 | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 90.0 °C | 194 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 138 - 149 °C | 280 - 300 °F | |
| Zone 2 | 149 - 163 °C | 300 - 325 °F | |
| Zone 3 | 191 - 204 °C | 375 - 400 °F | |
| Zone 4-x | 204 - 218 °C | 400 - 425 °F | |
| Adapter Temperature | 204 - 218 °C | 400 - 425 °F | |
| Die Temperature | 204 - 218 °C | 400 - 425 °F | |
| Melt Temperature | 204 - 218 °C | 400 - 425 °F | |