- 熔體流動速率 [g/10min]: 22.0
- 密度 [g/cm3]: 0.9235
- 彎曲模量 [MPa]: 0.303
- 脆化溫度 [℃]: -35.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9235 g/cc | 0.03336 lb/in3 | ASTM D1505 |
| Particle Mesh Size | 16 Mesh | 16 Mesh | Irregular shape. ETM = Equistar Test Method; ETM Malvern |
| Melt Flow | 22 g/10 min | 22 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 53 | 53 | ASTM D2240 |
| Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D638 |
| Elongation at Break | 150 % | 150 % | ASTM D638 |
| Flexural Modulus | 0.303 GPa | 44.0 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 110 °C | 230 °F | ASTM D3418 |
| Vicat Softening Point | 96.0 °C | 205 °F | ASTM D1525 |
| Brittleness Temperature | -35.0 °C | -31.0 °F | ASTM D746 |