- 熔體流動速率 [g/10min]: 0.75
- 密度 [g/cm3]: 0.92
- 拉伸強度 [MPa]: 11.7
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | 10% Igepal?, F50; ASTM D1693 |
| Melt Flow | 0.75 g/10 min | 0.75 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 57 | 57 | ASTM D2240 |
| Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D638 |
| Tensile Strength, Yield | 11.7 MPa | 1700 psi | ASTM D638 |
| Elongation at Break | 650 % | 650 % | ASTM D638 |
| 1% Secant Modulus | 345 MPa | 50000 psi | ASTM D790 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.29 | 2.29 | ASTM D1531 |
| Dissipation Factor | 0.000060 | 0.000060 | ASTM D1531 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 154 - 163 °C | 310 - 325 °F | |
| Zone 2 | 177 - 193 °C | 350 - 380 °F | |
| Zone 3 | 193 - 210 °C | 380 - 410 °F | |
| Zone 4-x | 204 - 218 °C | 400 - 425 °F | |
| Adapter Temperature | 204 - 218 °C | 400 - 425 °F | |
| Die Temperature | 204 - 218 °C | 400 - 425 °F | |