- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in3 | ASTM D1505 | ||
| Thickness | 1.00 microns | 0.0394 mil | 2.5:1 blow-up ratio | ||
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D-1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 10.3 MPa | 1490 psi | ASTM D-882 | ||
| Film Tensile Strength at Yield, TD | 10.5 MPa | 1530 psi | ASTM D-882 | ||
| Film Elongation at Break, MD | 595 % | 595 % | ASTM D-882 | ||
| Film Elongation at Break, TD | 795 % | 795 % | ASTM D-882 | ||
| Elmendorf Tear Strength MD | 110 g | 110 g | ASTM D-1922 | ||
| Elmendorf Tear Strength TD | 490 g | 490 g | ASTM D-1922 | ||
| Dart drop Test | 90.0 g | 0.198 lb | ASTM D-1709A | ||
| Film Tensile Strength at Break, MD | 38.7 MPa | 5620 psi | ASTM D-882 | ||
| Film Tensile Strength at Break, TD | 28.3 MPa | 4100 psi | ASTM D-882 | ||
| 1% Secant Modulus, MD | 208 MPa | 30200 psi | ASTM D-882 | ||
| 1% Secant Modulus, TD | 227 MPa | 32900 psi | ASTM D-882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 18.5 % | 18.5 % | ASTM D-1003 | ||
| Gloss | 35 % | 35 % | ASTM D-2457 | ||
| Descriptive Properties | |||||
| process | Film | ||||