- 熔體流動速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.9
- 缺口沖擊強度: 56.0
- 拉伸強度 [MPa]: 9.0
- 彎曲強度 [MPa]: 9.8
- 脆化溫度 [℃]: -70.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 - 0.960 g/cc | 0.0325 - 0.0347 lb/in3 | Average value: 0.920 g/cc Grade Count:278 |
| Moisture Vapor Transmission | 0.240 - 0.470 cc-mm/m2-24hr-atm | 0.610 - 1.19 cc-mil/100 in2-24hr-atm | Average value: 0.410 cc-mm/m2-24hr-atm Grade Count:21 |
| Water Vapor Transmission | 6.00 - 8.00 g/m2/day | 0.386 - 0.515 g/100 in2/day | Average value: 7.33 g/m2/day Grade Count:3 |
| Oxygen Transmission | 0.720 - 236 cc-mm/m2-24hr-atm | 1.83 - 599 cc-mil/100 in2-24hr-atm | Average value: 211 cc-mm/m2-24hr-atm Grade Count:19 |
| Oxygen Transmission Rate | 3500 - 5000 cc/m2/day | 225 - 322 cc/100 in2/day | Average value: 4500 cc/m2/day Grade Count:3 |
| Viscosity | 37000 - 79000 cP @Temperature 190 - 190 °C | 37000 - 79000 cP @Temperature 374 - 374 °F | Average value: 60000 cP Grade Count:1 |
| 37000 - 79000 cP @Shear Rate 300 - 5000 1/s | 37000 - 79000 cP @Shear Rate 300 - 5000 1/s | Average value: 60000 cP Grade Count:1 | |
| Environmental Stress Crack Resistance | >= 1000 hour @Temperature 50.0 - 50.0 °C | >= 1000 hour @Temperature 122 - 122 °F | Average value: 1000 hour Grade Count:5 |
| Thickness | 8.00 - 76.2 microns | 0.315 - 3.00 mil | Average value: 31.1 microns Grade Count:153 |
| Melt Flow | 0.200 - 123 g/10 min | 0.200 - 123 g/10 min | Average value: 3.50 g/10 min Grade Count:241 |
| Base Resin Melt Index | 0.700 - 3.50 g/10 min | 0.700 - 3.50 g/10 min | Average value: 1.71 g/10 min Grade Count:16 |
| Antiblock Level | 625 - 9000 ppm | 625 - 9000 ppm | Average value: 5210 ppm Grade Count:23 |
| Slip Level | 0.000 - 1700 ppm | 0.000 - 1700 ppm | Average value: 1160 ppm Grade Count:19 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 9.80 - 37.3 MPa | 1420 - 5410 psi | Average value: 23.1 MPa Grade Count:25 |
| Film Tensile Strength at Yield, MD | 5.00 - 74.0 MPa | 725 - 10700 psi | Average value: 11.7 MPa Grade Count:123 |
| Film Tensile Strength at Yield, TD | 5.00 - 77.0 MPa | 725 - 11200 psi | Average value: 11.7 MPa Grade Count:123 |
| Tensile Strength, Yield | 9.00 - 22.1 MPa | 1310 - 3210 psi | Average value: 12.5 MPa Grade Count:34 |
| Film Elongation at Break, MD | 80.0 - 1460 % | 80.0 - 1460 % | Average value: 648 % Grade Count:250 |
| Film Elongation at Break, TD | 460 - 1710 % | 460 - 1710 % | Average value: 836 % Grade Count:230 |
| Film Elongation at Yield, MD | 435 - 640 % | 435 - 640 % | Average value: 516 % Grade Count:6 |
| Film Elongation at Yield, TD | 670 - 890 % | 670 - 890 % | Average value: 763 % Grade Count:6 |
| Elongation at Break | 8.00 - 1000 % | 8.00 - 1000 % | Average value: 762 % Grade Count:35 |
| Modulus of Elasticity | 0.0110 - 0.413 GPa | 1.60 - 59.9 ksi | Average value: 0.179 GPa Grade Count:28 |
| Secant Modulus | 0.115 - 0.230 GPa | 16.7 - 33.4 ksi | Average value: 0.167 GPa Grade Count:5 |
| Secant Modulus, MD | 0.0103 - 0.717 GPa | 1.49 - 104 ksi | Average value: 0.195 GPa Grade Count:195 |
| Secant Modulus, TD | 0.0106 - 0.869 GPa | 1.54 - 126 ksi | Average value: 0.221 GPa Grade Count:195 |
| Izod Impact, Notched (ISO) | 56.0 - 56.0 kJ/m2 @Temperature -50.0 - -50.0 °C | 26.6 - 26.6 ft-lb/in2 @Temperature -58.0 - -58.0 °F | Average value: 56.0 kJ/m2 Grade Count:1 |
| Puncture Energy | 0.452 - 10.5 J | 0.333 - 7.74 ft-lb | Average value: 2.63 J Grade Count:43 |
| Coefficient of Friction | 0.100 - 2.00 | 0.100 - 2.00 | Average value: 0.559 Grade Count:70 |
| Coefficient of Friction, Static | 0.170 - 1.00 | 0.170 - 1.00 | Average value: 0.714 Grade Count:5 |
| Tear Strength Test | 16.0 - 22.0 | 16.0 - 22.0 | Average value: 20.0 Grade Count:6 |
| Elmendorf Tear Strength MD | 12.0 - 1080 g | 12.0 - 1080 g | Average value: 243 g Grade Count:112 |
| Elmendorf Tear Strength TD | 25.0 - 1470 g | 25.0 - 1470 g | Average value: 515 g Grade Count:114 |
| Elmendorf Tear Strength, MD | 0.0750 - 35.0 g/micron | 1.91 - 889 g/mil | Average value: 9.98 g/micron Grade Count:178 |
| Elmendorf Tear Strength, TD | 0.275 - 135 g/micron | 6.99 - 3430 g/mil | Average value: 21.7 g/micron Grade Count:178 |
| Dart drop Total Energy | 570 - 890 J/cm | 1.07 - 1.67 ft-lb/mil | Average value: 656 J/cm Grade Count:7 |
| Dart Drop | 1.57 - 59.1 g/micron | 40.0 - 1500 g/mil | Average value: 9.00 g/micron Grade Count:167 |
| Dart drop Test | 30.0 - 1350 g | 0.0662 - 2.98 lb | Average value: 258 g Grade Count:161 |
| Seal Strength | 1800 - 2400 g/25 mm | 1800 - 2400 g/in | Average value: 2070 g/25 mm Grade Count:12 |
| Film Tensile Strength at Break, MD | 9.65 - 82.7 MPa | 1400 - 12000 psi | Average value: 44.3 MPa Grade Count:263 |
| Film Tensile Strength at Break, TD | 7.24 - 55.1 MPa | 1050 - 7990 psi | Average value: 33.4 MPa Grade Count:243 |
| Heat Seal Strength Initiation Temperature | 72.0 - 102 °C | 162 - 216 °F | Average value: 96.6 °C Grade Count:10 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 116 - 128 °C | 241 - 262 °F | Average value: 123 °C Grade Count:56 |
| Crystallization Temperature | 104 - 115 °C | 219 - 239 °F | Average value: 110 °C Grade Count:7 |
| Vicat Softening Point | 65.0 - 123 °C | 149 - 253 °F | Average value: 101 °C Grade Count:63 |
| Brittleness Temperature | -70.0 °C | -94.0 °F | Average value: -70.0 °C Grade Count:9 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.700 - 80.0 % | 0.700 - 80.0 % | Average value: 14.4 % Grade Count:249 |
| Gloss | 3.00 - 155 % | 3.00 - 155 % | Average value: 64.3 % Grade Count:242 |
| Transmission, Visible | 90.0 % | 90.0 % | Average value: 90.0 % Grade Count:5 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 90.0 - 274 °C | 194 - 525 °F | Average value: 219 °C Grade Count:32 |
| Melt Temperature | 149 - 310 °C | 300 - 590 °F | Average value: 221 °C Grade Count:81 |
| Die Opening | 0.0810 - 0.254 cm | 0.0319 - 0.100 in | Average value: 0.172 cm Grade Count:13 |
| 0.180 - 0.250 cm @Temperature 200 - 220 °C | 0.0709 - 0.0984 in @Temperature 392 - 428 °F | Average value: 0.215 cm Grade Count:1 | |
| Extruder Size | 6.35 cm | 2.50 in | Average value: 6.35 cm Grade Count:3 |
| Blow-up Ratio (BUR) | 1.50 - 4.00 | 1.50 - 4.00 | Average value: 2.48 Grade Count:32 |