- 拉伸強度 [MPa]: 15.9
- 彎曲模量 [MPa]: 0.538
- 熱變形溫度 [℃]: 49.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.935 g/cc | 0.935 g/cc | ASTM D792 | ||
| ESCR 100% Igepal? | >= 1000 hour | >= 1000 hour | ASTM D1693 | ||
| Melt Index of Compound | 5.5 - 7.0 g/10 min | 5.5 - 7.0 g/10 min | 2.16/190; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | 2"/min; ASTM D638 | ||
| Elongation at Break | 400 % | 400 % | 2"/min; ASTM D638 | ||
| Flexural Modulus | 0.538 GPa | 78.0 ksi | at 1% secant modulus; ASTM D790 | ||
| Impact Test | 54.2 J @Thickness 3.17 mm, Temperature -40.0 °C | 40.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | ARM impact | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| UV Stabilization | UV-8 | ||||