- 熔體流動速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.87
- 缺口沖擊強度: 5.0
- 拉伸強度 [MPa]: 7.3
- 彎曲強度 [MPa]: 7.93
- 彎曲模量 [MPa]: 0.0165
- 熱變形溫度 [℃]: 42.0
- 脆化溫度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.870 - 1.86 g/cc | 0.0314 - 0.0672 lb/in3 | Average value: 0.934 g/cc Grade Count:104 |
| Viscosity | 42.0 - 300000 cP @Temperature 190 - 230 °C | 42.0 - 300000 cP @Temperature 374 - 446 °F | Average value: 40700 cP Grade Count:13 |
| 42.0 - 300000 cP @Shear Rate 300 - 5000 1/s | 42.0 - 300000 cP @Shear Rate 300 - 5000 1/s | Average value: 40700 cP Grade Count:13 | |
| Environmental Stress Crack Resistance | 1.00 - 1000 hour | 1.00 - 1000 hour | Average value: 221 hour Grade Count:32 |
| >= 1000 hour @Temperature 50.0 - 50.0 °C | >= 1000 hour @Temperature 122 - 122 °F | Average value: 668 hour Grade Count:2 | |
| 4.00 - 4.00 hour @Temperature 50.0 - 50.0 °C | 4.00 - 4.00 hour @Temperature 122 - 122 °F | Average value: 668 hour Grade Count:1 | |
| 4.00 - 4.00 hour @Thickness 3.80 - 3.80 mm | 4.00 - 4.00 hour @Thickness 0.150 - 0.150 in | Average value: 668 hour Grade Count:1 | |
| Thickness | 25.4 - 38.1 microns | 1.00 - 1.50 mil | Average value: 32.9 microns Grade Count:11 |
| Linear Mold Shrinkage | 0.0150 - 0.0200 cm/cm | 0.0150 - 0.0200 in/in | Average value: 0.0170 cm/cm Grade Count:8 |
| Melt Flow | 0.800 - 150 g/10 min | 0.800 - 150 g/10 min | Average value: 28.6 g/10 min Grade Count:101 |
| Spiral Flow | 32.0 - 67.8 cm | 12.6 - 26.7 in | Average value: 45.7 cm Grade Count:15 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 44.0 - 70.0 | 44.0 - 70.0 | Average value: 54.7 Grade Count:44 |
| Tensile Strength, Ultimate | 7.93 - 45.5 MPa | 1150 - 6600 psi | Average value: 12.6 MPa Grade Count:38 |
| Film Tensile Strength at Yield, MD | 1.31 - 12.5 MPa | 190 - 1810 psi | Average value: 9.65 MPa Grade Count:9 |
| Film Tensile Strength at Yield, TD | 10.3 - 13.0 MPa | 1500 - 1890 psi | Average value: 12.0 MPa Grade Count:7 |
| Tensile Strength, Yield | 7.30 - 42.0 MPa | 1060 - 6090 psi | Average value: 16.2 MPa Grade Count:74 |
| Film Elongation at Break, MD | 460 - 1000 % | 460 - 1000 % | Average value: 677 % Grade Count:25 |
| Film Elongation at Break, TD | 540 - 1100 % | 540 - 1100 % | Average value: 769 % Grade Count:23 |
| Elongation at Break | 25.0 - 1100 % | 25.0 - 1100 % | Average value: 455 % Grade Count:61 |
| Elongation at Yield | 8.00 - 30.0 % | 8.00 - 30.0 % | Average value: 14.5 % Grade Count:15 |
| Modulus of Elasticity | 0.140 - 1.57 GPa | 20.3 - 227 ksi | Average value: 0.463 GPa Grade Count:26 |
| Flexural Modulus | 0.0165 - 0.827 GPa | 2.40 - 120 ksi | Average value: 0.405 GPa Grade Count:60 |
| Secant Modulus | 0.230 - 0.689 GPa | 33.4 - 100 ksi | Average value: 0.431 GPa Grade Count:10 |
| Secant Modulus, MD | 0.179 - 0.207 GPa | 26.0 - 30.0 ksi | Average value: 0.201 GPa Grade Count:5 |
| Secant Modulus, TD | 0.221 - 0.238 GPa | 32.0 - 34.5 ksi | Average value: 0.234 GPa Grade Count:5 |
| Izod Impact, Notched | 5.00 - 8.01 J/cm | 9.37 - 15.0 ft-lb/in | Average value: 6.00 J/cm Grade Count:3 |
| Izod Impact, Notched (ISO) | 23.0 - 97.0 kJ/m2 @Temperature -50.0 - -50.0 °C | 10.9 - 46.2 ft-lb/in2 @Temperature -58.0 - -58.0 °F | Average value: 44.5 kJ/m2 Grade Count:8 |
| Tensile Impact Strength | 75.0 - 365 kJ/m2 | 35.7 - 174 ft-lb/in2 | Average value: 241 kJ/m2 Grade Count:7 |
| Dart Drop, Total Energy | 2.44 J | 1.80 ft-lb | Average value: 2.44 J Grade Count:4 |
| Coefficient of Friction | 0.120 - 0.500 | 0.120 - 0.500 | Average value: 0.235 Grade Count:4 |
| Coefficient of Friction, Static | 0.200 - 0.580 | 0.200 - 0.580 | Average value: 0.310 Grade Count:4 |
| Elmendorf Tear Strength MD | 260 - 600 g | 260 - 600 g | Average value: 514 g Grade Count:12 |
| Elmendorf Tear Strength TD | 490 - 900 g | 490 - 900 g | Average value: 729 g Grade Count:12 |
| Elmendorf Tear Strength, MD | 2.00 - 15.0 g/micron | 50.8 - 381 g/mil | Average value: 7.72 g/micron Grade Count:11 |
| Elmendorf Tear Strength, TD | 7.30 - 27.6 g/micron | 185 - 701 g/mil | Average value: 16.8 g/micron Grade Count:11 |
| Dart Drop | 3.00 - 19.7 g/micron | 76.2 - 500 g/mil | Average value: 6.47 g/micron Grade Count:12 |
| Dart drop Test | 290 - 1000 g | 0.639 - 2.20 lb | Average value: 570 g Grade Count:12 |
| Film Tensile Strength at Break, MD | 21.0 - 56.5 MPa | 3050 - 8200 psi | Average value: 38.7 MPa Grade Count:23 |
| Film Tensile Strength at Break, TD | 16.0 - 47.0 MPa | 2320 - 6820 psi | Average value: 31.7 MPa Grade Count:23 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 75.0 - 136 °C | 167 - 277 °F | Average value: 116 °C Grade Count:42 |
| Crystallization Temperature | 106 - 111 °C | 223 - 232 °F | Average value: 107 °C Grade Count:6 |
| Deflection Temperature at 0.46 MPa (66 psi) | 42.0 - 75.0 °C | 108 - 167 °F | Average value: 51.1 °C Grade Count:12 |
| Deflection Temperature at 1.8 MPa (264 psi) | 35.0 - 44.0 °C | 95.0 - 111 °F | Average value: 37.4 °C Grade Count:4 |
| Vicat Softening Point | 41.1 - 130 °C | 106 - 266 °F | Average value: 95.7 °C Grade Count:63 |
| Brittleness Temperature | -76.1 - 76.0 °C | -105 - 169 °F | Average value: -64.5 °C Grade Count:38 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.50 - 55.0 % | 1.50 - 55.0 % | Average value: 19.2 % Grade Count:17 |
| Gloss | 45.0 - 94.0 % | 45.0 - 94.0 % | Average value: 67.2 % Grade Count:11 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 149 - 154 °C | 300 - 310 °F | Average value: 150 °C Grade Count:8 |
| Nozzle Temperature | 149 - 275 °C | 300 - 527 °F | Average value: 219 °C Grade Count:13 |
| Melt Temperature | 95.0 - 302 °C | 203 - 575 °F | Average value: 186 °C Grade Count:31 |
| Mold Temperature | 10.0 - 60.0 °C | 50.0 - 140 °F | Average value: 36.6 °C Grade Count:7 |
| Die Opening | 0.0810 - 0.254 cm | 0.0319 - 0.100 in | Average value: 0.169 cm Grade Count:6 |
| Blow-up Ratio (BUR) | 1.50 - 3.00 | 1.50 - 3.00 | Average value: 2.31 Grade Count:8 |
| Injection Pressure | 2.76 - 100 MPa | 400 - 14500 psi | Average value: 38.0 MPa Grade Count:5 |