- 密度 [g/cm3]: 1.45
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in3 | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 110 MPa | 16000 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.80 % | 1.80 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 9.00 GPa | 1310 ksi | 1mm/min; ISO 527-2/1A |
| Charpy Impact Unnotched | 4.00 J/cm2 | 19.0 ft-lb/in2 | ISO 179/1eU |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 46.0 kV/mm | 1170 kV/in | IEC 60243-1 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 285 °C | 545 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 120 - 140 °C | 248 - 284 °F | Cavity temperature |
| Melt Temperature | 295 - 310 °C | 563 - 590 °F | |
| Drying Temperature | 95.0 °C | 203 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
| Moisture Content | 0.0300 % | 0.0300 % | Necessary low maximum residual |