- 密度 [g/cm3]: 1.65
- 彎曲模量 [MPa]: 10.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in3 | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 100 MPa | 14500 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.20 % | 1.20 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 10.0 GPa | 1450 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 10.5 GPa | 1520 ksi | ISO 178 |
| Charpy Impact Unnotched | 2.00 J/cm2 | 9.52 ft-lb/in2 | ISO 179/1eU |
| Charpy Impact, Notched | 0.700 J/cm2 | 3.33 ft-lb/in2 | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 0.790 mm | V-0 @Thickness 0.0311 in | UL94 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 80.0 - 120 °C | 176 - 248 °F | Cavity temperature |
| Melt Temperature | 295 - 310 °C | 563 - 590 °F | |
| Drying Temperature | 95.0 °C | 203 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
| Moisture Content | 0.0300 % | 0.0300 % | Necessary low maximum residual |