- 密度 [g/cm3]: 1.55
- 缺口沖擊強度: 8.0
- 彎曲模量 [MPa]: 10.7
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in3 | ISO 1183 | ||
| Filler Content | 40 % | 40 % | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527 | ||
| Elongation at Break | 1.8 % | 1.8 % | ISO 527 | ||
| Tensile Modulus | 11.5 GPa @Temperature 23.0 °C | 1670 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 | ||
| Flexural Modulus | 10.7 GPa | 1550 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 8.00 kJ/m2 @Temperature 23.0 °C | 3.81 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | ||
| Charpy Impact Unnotched | 5.00 J/cm2 @Temperature 23.0 °C | 23.8 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.800 J/cm2 @Temperature 23.0 °C | 3.81 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 283 °C | 541 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 264 °C | 507 °F | ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 300 °C | 572 °F | Optimum | ||
| 295 - 310 °C | 563 - 590 °F | ||||
| Mold Temperature | 100 °C | 212 °F | Optimum | ||
| 80.0 - 120 °C | 176 - 248 °F | ||||
| Drying Temperature | 95.0 °C | 203 °F | |||
| Dry Time | 4 - 6 hour | 4 - 6 hour | Dehumidified Dryer | ||
| Moisture Content | <= 0.030 % | <= 0.030 % | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Drying Recommended | Yes | ||||
| Filler | Glass fiber reinforcement | ||||
| Forms | Pellets | ||||
| Generic | PCT | ||||
| Part Marking Code | >PCT-GF40< | ISO 11469 | |||
| Polymer Family | Polyester | ||||
| Polymer Type | PCT | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Electrical Resins | ||||
| Glass Reinforced Resins | |||||
| Region Available | Americas | ||||
| Asia/Pacific | |||||
| Europe | |||||
| Resin Identification | PCT-GF40 | ISO 1043 | |||