- 密度 [g/cm3]: 1.45
- 缺口沖擊強度: 0.75
- 彎曲強度 [MPa]: 117.0
- 彎曲模量 [MPa]: 8.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D 792 | ||
| Density | 1.45 g/cc | 0.0524 lb/in3 | ISO 1183 | ||
| Filler Content | 30 % | 30 % | |||
| Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Thickness 2.00 mm | 0.0025 in/in @Thickness 0.0787 in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 70 | 70 | ASTM D 785 | ||
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527 | ||
| Tensile Strength, Ultimate | 117 MPa @Temperature 23.0 °C | 17000 psi @Temperature 73.4 °F | ASTM D 638 | ||
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 | ||
| 2.3 % @Temperature 23.0 °C | 2.3 % @Temperature 73.4 °F | ASTM D 638 | |||
| Tensile Modulus | 8.90 GPa @Temperature 23.0 °C | 1290 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 180 MPa | 26100 psi | ASTM D 790 | ||
| 188 MPa | 27300 psi | ISO 178 | |||
| Flexural Modulus | 8.00 GPa | 1160 ksi | ISO 178 | ||
| 8.50 GPa | 1230 ksi | ASTM D 790 | |||
| Izod Impact, Notched | 0.750 J/cm @Temperature 23.0 °C | 1.41 ft-lb/in @Temperature 73.4 °F | ASTM D 256 | ||
| Izod Impact, Unnotched | 7.30 J/cm @Temperature 23.0 °C | 13.7 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 | ||
| Izod Impact, Notched (ISO) | 8.00 kJ/m2 @Temperature 23.0 °C | 3.81 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | ||
| Charpy Impact Unnotched | 5.00 J/cm2 @Temperature 23.0 °C | 23.8 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.800 J/cm2 @Temperature 23.0 °C | 3.81 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D 257 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D 257 | ||
| Dielectric Constant | 3.2 @Frequency 10000 Hz, Temperature 23.0 °C | 3.2 @Frequency 10000 Hz, Temperature 73.4 °F | ASTM D 150 | ||
| 3.2 @Frequency 100000 Hz, Temperature 23.0 °C | 3.2 @Frequency 100000 Hz, Temperature 73.4 °F | ASTM D 150 | |||
| 3.2 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.2 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | ASTM D 150 | |||
| 3.3 @Frequency 1000 Hz, Temperature 23.0 °C | 3.3 @Frequency 1000 Hz, Temperature 73.4 °F | ASTM D 150 | |||
| Dielectric Strength | 16.1 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C | 409 kV/in @Thickness 0.126 in, Temperature 73.4 °F | 500 V/s, Short Time; ASTM D149 | ||
| Dissipation Factor | 0.0070 @Frequency 10000 Hz | 0.0070 @Frequency 10000 Hz | ASTM D 150 | ||
| 0.010 @Frequency 100000 Hz | 0.010 @Frequency 100000 Hz | ASTM D 150 | |||
| 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | ASTM D 150 | |||
| 0.018 @Frequency 1000 Hz | 0.018 @Frequency 1000 Hz | ASTM D 150 | |||
| Comparative Tracking Index | 560 V | 560 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 283 °C | 541 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 262 °C | 504 °F | ISO 75-1/-2 | ||
| 262 °C | 504 °F | ASTM D 648 | |||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | IEC 60695-11-10 | |||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 300 °C | 572 °F | Optimum | ||
| 295 - 310 °C | 563 - 590 °F | ||||
| Mold Temperature | 100 °C | 212 °F | Optimum | ||
| 80.0 - 120 °C | 176 - 248 °F | ||||
| Drying Temperature | 95.0 °C | 203 °F | |||
| Dry Time | 4 - 6 hour | 4 - 6 hour | Dehumidified Dryer | ||
| Moisture Content | <= 0.030 % | <= 0.030 % | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Drying Recommended | Yes | ||||
| Features | Electrical Properties, Good | ||||
| Filler | Glass fiber reinforcement | ||||
| Forms | Pellets | ||||
| Generic | PCT | ||||
| Part Marking Code | >PCT-GF30< | ISO 11469 | |||
| Polymer Family | Polyester | ||||
| Polymer Type | PCT | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Electrical Resins | ||||
| Glass Reinforced Resins | |||||
| Region Available | Americas | ||||
| Asia/Pacific | |||||
| Europe | |||||
| Resin Identification | PCT-GF30 | ISO 1043 | |||
| Uses | Connectors | ||||
| E/E Applications | |||||