- 密度 [g/cm3]: 1.45
- 缺口沖擊強度: 7.0
- 彎曲模量 [MPa]: 7.80
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in3 | ISO 1183 | ||
| Filler Content | 30 % | 30 % | |||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 2.00 mm | 0.0080 in/in @Thickness 0.0787 in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527 | ||
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 | ||
| Tensile Modulus | 8.70 GPa @Temperature 23.0 °C | 1260 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 | ||
| Flexural Modulus | 7.80 GPa | 1130 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 @Temperature 23.0 °C | 3.33 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | ||
| Charpy Impact Unnotched | 4.00 J/cm2 @Temperature 23.0 °C | 19.0 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.700 J/cm2 @Temperature 23.0 °C | 3.33 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 283 °C | 541 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 258 °C | 496 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | IEC 60695-11-10 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL94 | |||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 300 °C | 572 °F | Optimum | ||
| 295 - 310 °C | 563 - 590 °F | ||||
| Mold Temperature | 100 °C | 212 °F | Optimum | ||
| 80.0 - 120 °C | 176 - 248 °F | ||||
| Drying Temperature | 95.0 °C | 203 °F | |||
| Dry Time | 4 - 6 hour | 4 - 6 hour | Dehumidified Dryer | ||
| Moisture Content | <= 0.030 % | <= 0.030 % | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Drying Recommended | Yes | ||||
| Filler | Glass fiber reinforcement | ||||
| Forms | Pellets | ||||
| Generic | PCT | ||||
| Part Marking Code | >PCT-GF30< | ISO 11469 | |||
| Polymer Family | Polyester | ||||
| Polymer Type | PCT | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Electrical Resins | ||||
| Glass Reinforced Resins | |||||
| Region Available | Americas | ||||
| Asia/Pacific | |||||
| Europe | |||||
| Resin Identification | PCT-GF30 | ISO 1043 | |||