- 密度 [g/cm3]: 1.19
- 吸水率 [%]: 0.15
- 缺口沖擊強度: 0.49
- 拉伸強度 [MPa]: 42.0
- 斷裂伸長率 [%]: 49.0
- 彎曲強度 [MPa]: 39.2
- 彎曲模量 [MPa]: 1.67
- 硬度: 103.0
- 熱變形溫度 [℃]: 70.0
- 透光率 [%]: 82.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 - 1.23 g/cc | 0.0430 - 0.0444 lb/in3 | Average value: 1.21 g/cc Grade Count:19 |
| 1.08 - 1.08 g/cc @Temperature 285 - 285 °C | 0.0390 - 0.0390 lb/in3 @Temperature 545 - 545 °F | Average value: 1.08 g/cc Grade Count:2 | |
| Water Absorption | 0.150 % | 0.150 % | Average value: 0.150 % Grade Count:4 |
| Linear Mold Shrinkage | 0.00200 - 0.00600 cm/cm | 0.00200 - 0.00600 in/in | Average value: 0.00359 cm/cm Grade Count:17 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 103 - 107 | 103 - 107 | Average value: 105 Grade Count:12 |
| Tensile Strength, Ultimate | 39.2 - 53.0 MPa | 5690 - 7690 psi | Average value: 47.9 MPa Grade Count:13 |
| Tensile Strength, Yield | 42.0 - 50.0 MPa | 6090 - 7250 psi | Average value: 46.6 MPa Grade Count:18 |
| Elongation at Break | 50.0 - 340 % | 50.0 - 340 % | Average value: 211 % Grade Count:18 |
| Elongation at Yield | 4.00 - 5.00 % | 4.00 - 5.00 % | Average value: 4.51 % Grade Count:17 |
| Modulus of Elasticity | 1.30 - 2.13 GPa | 189 - 309 ksi | Average value: 1.77 GPa Grade Count:11 |
| Flexural Yield Strength | 49.0 - 69.0 MPa | 7110 - 10000 psi | Average value: 65.8 MPa Grade Count:13 |
| Flexural Modulus | 1.67 - 2.00 GPa | 242 - 290 ksi | Average value: 1.87 GPa Grade Count:13 |
| Izod Impact, Notched | 0.490 - 100 J/cm | 0.919 - 187 ft-lb/in | Average value: 1.50 J/cm Grade Count:13 |
| 0.400 - 0.750 J/cm @Temperature -40.0 - -40.0 °C | 0.749 - 1.41 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.493 J/cm Grade Count:12 | |
| Izod Impact, Unnotched | NB | NB | Grade Count:12 |
| NB - NB @Temperature -40.0 - -40.0 °C | NB - NB @Temperature -40.0 - -40.0 °F | Grade Count:12 | |
| Izod Impact, Notched (ISO) | 7.80 - 29.6 kJ/m2 | 3.71 - 14.1 ft-lb/in2 | Average value: 17.1 kJ/m2 Grade Count:7 |
| 4.80 - 6.30 kJ/m2 @Temperature -40.0 - -40.0 °C | 2.28 - 3.00 ft-lb/in2 @Temperature -40.0 - -40.0 °F | Average value: 5.44 kJ/m2 Grade Count:7 | |
| Charpy Impact Unnotched | NB | NB | Grade Count:6 |
| NB - NB @Temperature -30.0 - -30.0 °C | NB - NB @Temperature -22.0 - -22.0 °F | Grade Count:6 | |
| Charpy Impact, Notched | 0.830 - 6.10 J/cm2 | 3.95 - 29.0 ft-lb/in2 | Average value: 2.34 J/cm2 Grade Count:6 |
| 0.480 - 0.640 J/cm2 @Temperature -30.0 - -30.0 °C | 2.28 - 3.05 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 0.575 J/cm2 Grade Count:6 | |
| Puncture Energy | 38.0 - 71.0 J | 28.0 - 52.4 ft-lb | Average value: 48.4 J Grade Count:12 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 75.0 - 97.0 μm/m-°C | 41.7 - 53.9 μin/in-°F | Average value: 85.0 μm/m-°C Grade Count:7 |
| CTE, linear, Transverse to Flow | 60.0 - 78.0 μm/m-°C | 33.3 - 43.3 μin/in-°F | Average value: 69.2 μm/m-°C Grade Count:6 |
| Specific Heat Capacity | 1.34 J/g-°C | 0.320 BTU/lb-°F | Average value: 1.34 J/g-°C Grade Count:3 |
| 1.09 - 2.16 J/g-°C @Temperature 10.0 - 290 °C | 0.261 - 0.516 BTU/lb-°F @Temperature 50.0 - 554 °F | Average value: 1.58 J/g-°C Grade Count:2 | |
| Thermal Conductivity | 0.190 - 0.220 W/m-K | 1.32 - 1.53 BTU-in/hr-ft2-°F | Average value: 0.202 W/m-K Grade Count:5 |
| Melting Point | 222 - 225 °C | 432 - 437 °F | Average value: 224 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 - 89.0 °C | 158 - 192 °F | Average value: 74.0 °C Grade Count:18 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 - 78.0 °C | 149 - 172 °F | Average value: 66.2 °C Grade Count:19 |
| Vicat Softening Point | 77.0 - 86.0 °C | 171 - 187 °F | Average value: 81.9 °C Grade Count:11 |
| Glass Transition Temp, Tg | 82.0 - 87.0 °C | 180 - 189 °F | Average value: 84.0 °C Grade Count:8 |
| Flammability, UL94 | HB | HB | Grade Count:6 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.300 - 1.00 % | 0.300 - 1.00 % | Average value: 0.592 % Grade Count:12 |
| Transmission, Visible | 82.0 - 92.0 % | 82.0 - 92.0 % | Average value: 90.0 % Grade Count:14 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 230 - 295 °C | 446 - 563 °F | Average value: 268 °C Grade Count:17 |
| Mold Temperature | 15.0 - 38.0 °C | 59.0 - 100 °F | Average value: 22.9 °C Grade Count:11 |
| Drying Temperature | 70.0 - 71.0 °C | 158 - 160 °F | Average value: 70.1 °C Grade Count:11 |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Average value: 3.41 hour Grade Count:11 |