- 密度 [g/cm3]: 1.39
- 缺口沖擊強度: 0.75
- 斷裂伸長率 [%]: 150
- 彎曲強度 [MPa]: 97.0
- 彎曲模量 [MPa]: 6.50
- 熱變形溫度 [℃]: 268.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 - 1.65 g/cc | 0.0502 - 0.0596 lb/in3 | Average value: 1.52 g/cc Grade Count:15 |
| Filler Content | 30.0 % | 30.0 % | Average value: 30.0 % Grade Count:10 |
| Linear Mold Shrinkage | 0.00200 - 0.00300 cm/cm | 0.00200 - 0.00300 in/in | Average value: 0.00269 cm/cm Grade Count:8 |
| Linear Mold Shrinkage, Transverse | 0.00750 - 0.00900 cm/cm | 0.00750 - 0.00900 in/in | Average value: 0.00806 cm/cm Grade Count:8 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 65.0 - 119 | 65.0 - 119 | Average value: 84.7 Grade Count:3 |
| Tensile Strength, Ultimate | 97.0 - 125 MPa | 14100 - 18100 psi | Average value: 113 MPa Grade Count:15 |
| Elongation at Break | 1.20 - 3.10 % | 1.20 - 3.10 % | Average value: 2.05 % Grade Count:15 |
| Modulus of Elasticity | 7.40 - 11.0 GPa | 1070 - 1600 ksi | Average value: 9.35 GPa Grade Count:15 |
| Flexural Yield Strength | 150 - 188 MPa | 21800 - 27300 psi | Average value: 171 MPa Grade Count:15 |
| Flexural Modulus | 6.50 - 10.5 GPa | 943 - 1520 ksi | Average value: 8.61 GPa Grade Count:15 |
| Izod Impact, Notched | 0.750 - 1.50 J/cm | 1.41 - 2.81 ft-lb/in | Average value: 1.05 J/cm Grade Count:3 |
| 1.10 - 1.10 J/cm @Temperature -40.0 - -40.0 °C | 2.06 - 2.06 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 1.10 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 6.90 - 9.10 J/cm | 12.9 - 17.0 ft-lb/in | Average value: 7.77 J/cm Grade Count:3 |
| Izod Impact, Notched (ISO) | 6.00 - 10.0 kJ/m2 | 2.86 - 4.76 ft-lb/in2 | Average value: 7.91 kJ/m2 Grade Count:11 |
| Charpy Impact Unnotched | 2.00 - 5.50 J/cm2 | 9.52 - 26.2 ft-lb/in2 | Average value: 3.82 J/cm2 Grade Count:14 |
| Charpy Impact, Notched | 0.600 - 1.00 J/cm2 | 2.86 - 4.76 ft-lb/in2 | Average value: 0.770 J/cm2 Grade Count:15 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 - 1.00e+16 ohm-cm | 1.00e+15 - 1.00e+16 ohm-cm | Average value: 3.25e+15 ohm-cm Grade Count:4 |
| Surface Resistance | 1.00e+15 - 1.00e+16 ohm | 1.00e+15 - 1.00e+16 ohm | Average value: 5.50e+15 ohm Grade Count:4 |
| Dielectric Constant | 3.00 - 3.30 | 3.00 - 3.30 | Average value: 3.11 Grade Count:3 |
| Dielectric Strength | 16.1 - 35.0 kV/mm | 409 - 889 kV/in | Average value: 25.6 kV/mm Grade Count:6 |
| Dissipation Factor | 0.00200 - 0.0180 | 0.00200 - 0.0180 | Average value: 0.0101 Grade Count:3 |
| Comparative Tracking Index | 440 - 600 V | 440 - 600 V | Average value: 520 V Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 6.00 - 48.0 μm/m-°C | 3.33 - 26.7 μin/in-°F | Average value: 28.7 μm/m-°C Grade Count:3 |
| CTE, linear, Transverse to Flow | 85.0 - 100 μm/m-°C | 47.2 - 55.6 μin/in-°F | Average value: 91.7 μm/m-°C Grade Count:3 |
| Melting Point | 283 - 285 °C | 541 - 545 °F | Average value: 284 °C Grade Count:13 |
| Deflection Temperature at 0.46 MPa (66 psi) | 268 - 276 °C | 514 - 529 °F | Average value: 271 °C Grade Count:4 |
| Deflection Temperature at 1.8 MPa (264 psi) | 221 - 262 °C | 430 - 504 °F | Average value: 247 °C Grade Count:15 |
| UL RTI, Electrical | 150 °C | 302 °F | Average value: 150 °C Grade Count:4 |
| UL RTI, Mechanical without Impact | 140 - 150 °C | 284 - 302 °F | Average value: 149 °C Grade Count:4 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:13 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 80.0 - 220 °C | 176 - 428 °F | Average value: 121 °C Grade Count:5 |
| Melt Temperature | 295 - 310 °C | 563 - 590 °F | Average value: 301 °C Grade Count:15 |
| Mold Temperature | 80.0 - 175 °C | 176 - 347 °F | Average value: 109 °C Grade Count:13 |
| Drying Temperature | 70.0 - 150 °C | 158 - 302 °F | Average value: 98.7 °C Grade Count:15 |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Average value: 5.00 hour Grade Count:15 |
| Moisture Content | 0.0300 % | 0.0300 % | Average value: 0.0300 % Grade Count:14 |