- 密度 [g/cm3]: 1.44
- 缺口沖擊強度: 10.0
- 彎曲模量 [MPa]: 7.40
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in3 | ISO 1183 | ||
| Filler Content | 30 % | 30 % | |||
| Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Thickness 2.00 mm | 0.0025 in/in @Thickness 0.0787 in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm @Thickness 2.00 mm | 0.0075 in/in @Thickness 0.0787 in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 65 | 65 | ASTM D 785 | ||
| Tensile Strength at Break | 116 MPa | 16800 psi | ISO 527 | ||
| Elongation at Break | 2.8 % | 2.8 % | ISO 527 | ||
| Tensile Modulus | 8.40 GPa @Temperature 23.0 °C | 1220 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 175 MPa | 25400 psi | ISO 178 | ||
| Flexural Modulus | 7.40 GPa | 1070 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 @Temperature 23.0 °C | 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | ||
| Charpy Impact Unnotched | 5.50 J/cm2 @Temperature 23.0 °C | 26.2 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.00 J/cm2 @Temperature 23.0 °C | 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D 257 | ||
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D 257 | ||
| Dielectric Constant | 3.0 @Frequency 100000 Hz, Temperature 23.0 °C | 3.0 @Frequency 100000 Hz, Temperature 73.4 °F | ASTM D 150 | ||
| 3.0 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.0 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | ASTM D 150 | |||
| 3.1 @Frequency 10000 Hz, Temperature 23.0 °C | 3.1 @Frequency 10000 Hz, Temperature 73.4 °F | ASTM D 150 | |||
| 3.2 @Frequency 1000 Hz, Temperature 23.0 °C | 3.2 @Frequency 1000 Hz, Temperature 73.4 °F | ASTM D 150 | |||
| Dielectric Strength | 16.4 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C | 417 kV/in @Thickness 0.126 in, Temperature 73.4 °F | 500 V/s, Short Time; ASTM D149 | ||
| Dissipation Factor | 0.0090 @Frequency 10000 Hz | 0.0090 @Frequency 10000 Hz | ASTM D 150 | ||
| 0.0090 @Frequency 100000 Hz | 0.0090 @Frequency 100000 Hz | ASTM D 150 | |||
| 0.011 @Frequency 1.00e+6 Hz | 0.011 @Frequency 1.00e+6 Hz | ASTM D 150 | |||
| 0.011 @Frequency 1000 Hz | 0.011 @Frequency 1000 Hz | ASTM D 150 | |||
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 285 °C | 545 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 300 °C | 572 °F | Optimum | ||
| 295 - 310 °C | 563 - 590 °F | ||||
| Mold Temperature | 100 °C | 212 °F | Optimum | ||
| 80.0 - 120 °C | 176 - 248 °F | ||||
| Drying Temperature | 95.0 °C | 203 °F | |||
| Dry Time | 4 - 6 hour | 4 - 6 hour | Dehumidified Dryer | ||
| Moisture Content | <= 0.030 % | <= 0.030 % | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Drying Recommended | Yes | ||||
| Features | Electrical Properties, Good | ||||
| Toughness, Good | |||||
| Filler | Glass fiber reinforcement | ||||
| Forms | Pellets | ||||
| Generic | PCT | ||||
| Part Marking Code | >PCT-IGF30< | ISO 11469 | |||
| Polymer Family | Polyester | ||||
| Polymer Type | PCT | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Electrical Resins | ||||
| Glass Reinforced Resins | |||||
| Toughened Resins | |||||
| Region Available | Americas | ||||
| Asia/Pacific | |||||
| Europe | |||||
| Resin Identification | PCT-IGF30 | ISO 1043 | |||
| Uses | Connectors | ||||
| E/E Applications | |||||