- 密度 [g/cm3]: 1.38
- 吸水率 [%]: 0.05
- 缺口沖擊強度: 0.7
- 熱變形溫度 [℃]: 235.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in3 | |
| Water Absorption | 0.050 % | 0.050 % | 24 hrs at 23°C |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 2.00 mm | 0.0040 in/in @Thickness 0.0787 in | |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90 | 90 | |
| Tensile Strength at Break | 80.0 MPa | 11600 psi | |
| Elongation at Break | 3.1 % | 3.1 % | |
| Modulus of Elasticity | 4.20 GPa | 609 ksi | |
| Flexural Strength | 125 MPa | 18100 psi | |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 40.0 μm/m-°C @Temperature 20.0 °C | 22.2 μin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | 0.455 MPa |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 120 °C | 248 °F | |