- 熔體流動速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 0.17
- 缺口沖擊強度: 6.41
- 拉伸強度 [MPa]: 53.8
- 斷裂伸長率 [%]: 89.6
- 彎曲模量 [MPa]: 2.14
- 硬度: 117.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in3 | ASTM D792 |
| Water Absorption | 0.17 % @Time 86400 sec | 0.17 % @Time 24.0 hour | ASTM D570 |
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 265 °C | 12 g/10 min @Load 11.0 lb, Temperature 509 °F | ASTM D1238 |
| 28 g/10 min @Load 2.16 kg, Temperature 285 °C | 28 g/10 min @Load 4.76 lb, Temperature 545 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength, Yield | 53.8 MPa | 7800 psi | ASTM D638 |
| Elongation at Break | 120 % | 120 % | ASTM D638 |
| Flexural Yield Strength | 89.6 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 2.14 GPa | 310 ksi | ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm @Thickness 3.17 mm, Temperature -40.0 °C | 12.0 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F | ASTM D256 |
| 8.54 J/cm @Thickness 3.17 mm, Temperature 22.8 °C | 16.0 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F | ASTM D256 | |
| Dart Drop, Total Energy | 5.14 J @Temperature -40.0 °C | 3.79 ft-lb @Temperature -40.0 °F | ASTM D3763 |
| 5.31 J @Temperature 22.8 °C | 3.92 ft-lb @Temperature 73.0 °F | ASTM D3763 | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 7.00e+15 ohm-cm | 7.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 27.6 kV/mm | 700 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 63.0 μm/m-°C | 35.0 μin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C | 240 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |