- 密度 [g/cm3]: 1.58
- 吸水率 [%]: 0.06
- 缺口沖擊強度: 0.65
- 彎曲模量 [MPa]: 8.50
- 熱變形溫度 [℃]: 225.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in3 | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | 24 hrs at 23°C; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.00 mm | 0.0040 in/in @Thickness 0.118 in | MD |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 3.00 mm | 0.0090 in/in @Thickness 0.118 in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90 | 90 | ASTM D785 |
| Tensile Strength at Break | 142 MPa | 20600 psi | ASTM D638 |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D638 |
| Flexural Strength | 170 MPa | 24700 psi | ASTM D790 |
| Flexural Modulus | 8.50 GPa | 1230 ksi | ASTM D790 |
| Izod Impact, Notched | 0.650 J/cm | 1.22 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 24.0 kV/mm @Thickness 2.00 mm | 610 kV/in @Thickness 0.0787 in | ASTM D149 |
| Arc Resistance | 90 sec | 90 sec | Tungsten electrode; ASTM D495 |
| Comparative Tracking Index | 175 - 249 V | 175 - 249 V | IEC Pub1.112, class 3; IEC Method |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 35.0 μm/m-°C @Temperature 20.0 °C | 19.4 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Maximum Service Temperature, Air | 205 °C | 401 °F | Ball pressure temperature; ASTM UL746B |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 265 °C | 509 °F | Molding temperature |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 140 °C | 284 °F | |
| Dry Time | 3 hour | 3 hour | |