- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 0.2
- 缺口沖擊強(qiáng)度: 0.747
- 拉伸強(qiáng)度 [MPa]: 115.0
- 彎曲模量 [MPa]: 5.34
- 硬度: 110.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in3 | ASTM D792 |
| Water Absorption | 0.20 % @Time 86400 sec | 0.20 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0055 cm/cm @Thickness 3.17 mm | 0.0055 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 115 MPa | 16700 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Strength | 96.5 MPa | 14000 psi | ASTM D790 |
| Flexural Modulus | 5.34 GPa | 775 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm @Thickness 3.17 mm | 1.40 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 23.4 μm/m-°C | 13.0 μin/in-°F | ASTM D696 |
| Melting Point | 248 °C | 478 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | Unannealed; ASTM D648 |