- 熔體流動速率 [g/10min]: 15.0
- 密度 [g/cm3]: 1.46
- 缺口沖擊強度: 0.45
- 拉伸強度 [MPa]: 75.0
- 斷裂伸長率 [%]: 110
- 彎曲模量 [MPa]: 6.00
- 硬度: 120.0
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 | ||
| Density | 1.46 g/cc | 0.0527 lb/in3 | ISO 1183 | ||
| Filler Content | 15 % | 15 % | ASTM D229 | ||
| Viscosity | 145000 cP | 145000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 | ||
| Melt Flow | 15 g/10 min @Load 5.00 kg, Temperature 250 °C | 15 g/10 min @Load 11.0 lb, Temperature 482 °F | ISO 1133 | ||
| 20 g/10 min @Load 2.16 kg, Temperature 265 °C | 20 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D1238 | |||
| Melt Index of Compound | 5.0 g/10 min @Load 1.20 kg, Temperature 265 °C | 5.0 g/10 min @Load 2.65 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 | ||
| 11 g/10 min @Load 5.00 kg, Temperature 250 °C | 11 g/10 min @Load 11.0 lb, Temperature 482 °F | MVR [cm^3/10 min]; ASTM D1238 | |||
| 13 g/10 min @Load 2.16 kg, Temperature 265 °C | 13 g/10 min @Load 4.76 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 | |||
| 45 g/10 min @Load 5.00 kg, Temperature 265 °C | 45 g/10 min @Load 11.0 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 120 | 120 | ISO 2039-2 | ||
| Hardness, H358/30 | 142 MPa | 20600 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Type I, 5 mm/min; ASTM D638 | ||
| 75.0 MPa | 10900 psi | 5 mm/min; ISO 527 | |||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | Type I, 5 mm/min; ASTM D638 | ||
| 75.0 MPa | 10900 psi | 5 mm/min; ISO 527 | |||
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | ||
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |||
| 3.0 % | 3.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |||
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | ||
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |||
| Tensile Modulus | 7.20 GPa | 1040 ksi | 5 mm/min; ASTM D638 | ||
| 7.40 GPa | 1070 ksi | 1 mm/min; ISO 527 | |||
| Flexural Strength | 110 MPa | 16000 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | ||
| 125 MPa | 18100 psi | break, 2 mm/min; ISO 178 | |||
| Flexural Yield Strength | 110 MPa | 16000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| 125 MPa | 18100 psi | 2 mm/min; ISO 178 | |||
| Flexural Modulus | 6.00 GPa | 870 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| 6.30 GPa | 914 ksi | 2 mm/min; ISO 178 | |||
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in | ASTM D256 | ||
| 0.450 J/cm @Temperature 0.000 °C | 0.843 ft-lb/in @Temperature 32.0 °F | ASTM D256 | |||
| 0.450 J/cm @Temperature -30.0 °C | 0.843 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |||
| Izod Impact, Unnotched | 3.30 J/cm | 6.18 ft-lb/in | ASTM D4812 | ||
| 2.80 J/cm @Temperature -30.0 °C | 5.25 ft-lb/in @Temperature -22.0 °F | ASTM D4812 | |||
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | 80*10*4; ISO 180/1A | ||
| 5.00 kJ/m2 @Temperature 0.000 °C | 2.38 ft-lb/in2 @Temperature 32.0 °F | 80*10*4; ISO 180/1A | |||
| 5.00 kJ/m2 @Temperature -30.0 °C | 2.38 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 22.0 kJ/m2 | 10.5 ft-lb/in2 | 80*10*4; ISO 180/1U | ||
| 20.0 kJ/m2 @Temperature -30.0 °C | 9.52 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |||
| Charpy Impact Unnotched | 2.30 J/cm2 | 10.9 ft-lb/in2 | ISO 179/2C | ||
| 2.00 J/cm2 @Temperature -30.0 °C | 9.52 ft-lb/in2 @Temperature -22.0 °F | ISO 179/2C | |||
| Charpy Impact, Notched | 0.500 J/cm2 | 2.38 ft-lb/in2 | ISO 179/2C | ||
| 0.500 J/cm2 @Temperature -30.0 °C | 2.38 ft-lb/in2 @Temperature -22.0 °F | ISO 179/2C | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 | ||
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 | ||
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz | 3.3 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 3.3 @Frequency 1.00e+6 Hz | 3.3 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Dielectric Strength | 19.0 kV/mm @Thickness 3.20 mm | 483 kV/in @Thickness 0.126 in | in oil; ASTM D149 | ||
| 19.0 kV/mm @Thickness 3.20 mm | 483 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 | |||
| 28.0 kV/mm @Thickness 1.60 mm | 711 kV/in @Thickness 0.0630 in | in oil; ASTM D149 | |||
| 28.0 kV/mm @Thickness 1.60 mm | 711 kV/in @Thickness 0.0630 in | in oil; IEC 60243-1 | |||
| 38.0 kV/mm @Thickness 0.800 mm | 965 kV/in @Thickness 0.0315 in | in oil; IEC 60243-1 | |||
| 38.0 kV/mm @Thickness 0.800 mm | 965 kV/in @Thickness 0.0315 in | in oil; ASTM D149 | |||
| Dissipation Factor | 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 400 V | 400 V | IEC 60112 | ||
| 400 - 600 V | 400 - 600 V | UL 746A | |||
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A | ||
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 31.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 17.2 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | ||
| 46.0 μm/m-°C @Temperature 23.0 - 150 °C | 25.6 μin/in-°F @Temperature 73.4 - 302 °F | ISO 11359-2 | |||
| CTE, linear, Transverse to Flow | 63.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 35.0 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | ||
| 165 μm/m-°C @Temperature 23.0 - 150 °C | 91.7 μin/in-°F @Temperature 73.4 - 302 °F | ISO 11359-2 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf | ||
| 215 °C @Thickness 3.20 mm | 419 °F @Thickness 0.126 in | unannealed; ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | ||
| 190 °C @Thickness 3.20 mm | 374 °F @Thickness 0.126 in | unannealed; ASTM D648 | |||
| Vicat Softening Point | 196 °C | 385 °F | Rate B/50; ISO 306 | ||
| 200 °C | 392 °F | Rate B/120; ISO 306 | |||
| 202 °C | 396 °F | Rate B/50; ASTM D1525 | |||
| 215 °C | 419 °F | Rate A/50; ISO 306 | |||
| 220 °C | 428 °F | Rate A/50; ASTM D1525 | |||
| UL RTI, Electrical | 75.0 °C | 167 °F | UL 746B | ||
| UL RTI, Mechanical with Impact | 75.0 °C | 167 °F | UL 746B | ||
| UL RTI, Mechanical without Impact | 75.0 °C | 167 °F | UL 746B | ||
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL 94 by SABIC-IP | ||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL 94 | |||
| 5VA @Thickness 2.00 mm | 5VA @Thickness 0.0787 in | UL 94 | |||
| Glow Wire Test | 800 °C | 1470 °F | IEC 60695-2-13 | ||
| 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | IEC 60695-2-12 | |||
| Descriptive Properties | |||||
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 | |||