- 熔體流動速率 [g/10min]: 42.0
- 密度 [g/cm3]: 1.67
- 吸水率 [%]: 0.3
- 熱變形溫度 [℃]: 225.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.30 % | 0.30 % | Test Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 23°C/50% R.H.; Test Sim. to ISO 62 | ||
| Viscosity Test | 80 cm3/g | 80 cm3/g | Viscosity number; ISO 307, 1157, 1628 | ||
| Melt Flow | 42 g/10 min @Load 5.00 kg, Temperature 260 °C | 42 g/10 min @Load 11.0 lb, Temperature 500 °F | Calculated from MVR using melt density; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527-1/-2 | ||
| Elongation at Break | 1.7 % | 1.7 % | ISO 527-1/-2 | ||
| Tensile Modulus | 17.0 GPa | 2470 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 7.00 J/cm2 @Temperature -30.0 °C | 33.3 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| 7.00 J/cm2 @Temperature 23.0 °C | 33.3 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.10 J/cm2 @Temperature -30.0 °C | 5.23 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.20 J/cm2 @Temperature 23.0 °C | 5.71 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Impact | 775 | 775 | Puncture maximum force (N); ISO 6603-2 | ||
| Puncture Energy | 3.50 J | 2.58 ft-lb | ISO 6603-2 | ||
| Tensile Creep Modulus, 1 hour | 16500 MPa | 2.39e+6 psi | ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 15000 MPa | 2.18e+6 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 4.2 @Frequency 1.00e+6 Hz | 4.2 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.3 @Frequency 100 Hz | 4.3 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0020 @Frequency 100 Hz | 0.0020 @Frequency 100 Hz | IEC 60250 | ||
| 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 275 V | 275 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 μm/m-°C | 11.1 μin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 50.0 μm/m-°C | 27.8 μin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 150 °C | 302 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 210 °C | 410 °F | 50°C/h 50N; ISO 306 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | IEC 60695-11-10 | ||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | |||
| Oxygen Index | 21 % | 21 % | ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 °C | 518 °F | Injection Molding; ISO 294 | ||
| Mold Temperature | 90.0 °C | 194 °F | Injection Molding; ISO 10724 | ||
| Descriptive Properties | |||||
| Additives | Release agent | ||||
| Features | Heat stabilized or stable to heat | ||||
| Form | Pellets | ||||
| ISO Shortname | ISO 7792-1-PBT+PET,GHMR,09-160,GF45 | ||||