- 熔體流動速率 [g/10min]: 25.0
- 缺口沖擊強度: 10.0
- 彎曲模量 [MPa]: 11.0
- 熱變形溫度 [℃]: 250.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ISO 1183 | ||
| Bulk Density | 0.900 g/cc | 0.0325 lb/in3 | ISO 60 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 | ||
| 0.0020 cm/cm | 0.0020 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 | ||
| 0.0070 cm/cm | 0.0070 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 | |||
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 280 °C | 25 g/10 min @Load 4.76 lb, Temperature 536 °F | ISO 1133-1 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527-1, -2; 5 mm/min | ||
| Elongation at Break | 1.6 % | 1.6 % | ISO 527-1, -2; 5 mm/min | ||
| Tensile Modulus | 12.0 GPa | 1740 ksi | ISO 527-1, -2; 1 mm/min | ||
| Flexural Strength | 175 MPa @Strain 2.00 % | 25400 psi @Strain 2.00 % | 2 mm/min; ISO 178-A | ||
| Flexural Modulus | 11.0 GPa | 1600 ksi | 2 mm/min; ISO 178-A | ||
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m2 @Temperature 23.0 °C | <= 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 180-1A | ||
| <= 10.0 kJ/m2 @Temperature -30.0 °C | <= 4.76 ft-lb/in2 @Temperature -22.0 °F | ISO 180-1A | |||
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m2 @Temperature 23.0 °C | 16.7 ft-lb/in2 @Temperature 73.4 °F | ISO 180-1U | ||
| Charpy Impact, Notched | <= 1.00 J/cm2 @Temperature 23.0 °C | <= 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 179-1eA | ||
| <= 1.00 J/cm2 @Temperature -30.0 °C | <= 4.76 ft-lb/in2 @Temperature -22.0 °F | ISO 179-1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 μm/m-°C @Temperature 23.0 - 55.0 °C | 11.1 μin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1, -2 | ||
| CTE, linear, Transverse to Flow | 50.0 μm/m-°C @Temperature 23.0 - 55.0 °C | 27.8 μin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1, -2 | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1, -3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 220 °C @Load 5.10 kg | 428 °F @Load 11.2 lb | 120°C/hour; ISO 306 | ||
| Glow Wire Test | 750 °C @Diameter 0.800 mm | 1380 °F @Diameter 0.0315 in | GWFI; IEC 60695-2-12 | ||
| 750 °C @Diameter 1.50 mm | 1380 °F @Diameter 0.0591 in | GWFI; IEC 60695-2-12 | |||
| 750 °C @Diameter 3.00 mm | 1380 °F @Diameter 0.118 in | GWFI; IEC 60695-2-12 | |||
| 775 °C @Diameter 0.800 mm | 1430 °F @Diameter 0.0315 in | GWIT; IEC 60695-2-13 | |||
| 775 °C @Diameter 1.50 mm | 1430 °F @Diameter 0.0591 in | GWIT; IEC 60695-2-13 | |||
| 775 °C @Diameter 3.00 mm | 1430 °F @Diameter 0.118 in | GWIT; IEC 60695-2-13 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |||
| 280 °C | 536 °F | for test specimens; ISO 294 | |||
| Mold Temperature | 110 °C | 230 °F | for test specimens; ISO 294 | ||
| 100 - 130 °C | 212 - 266 °F | ||||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4 - 8 hour | 4 - 8 hour | |||
| Moisture Content | 0.00 - 0.020 % | 0.00 - 0.020 % | residual; Karl Fischer Test | ||
| Descriptive Properties | |||||
| ISO Shortname | ISO 7792-1-PET+PBT, GHMR, 07-120, (GF+MD)40 | ||||