- 缺口沖擊強度: 0.34
- 彎曲模量 [MPa]: 5.394
- 硬度: 110.0
- 熱變形溫度 [℃]: 235.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength | 98.0 MPa | 14200 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Strength | 152 MPa | 22000 psi | ASTM D790 |
| Flexural Modulus | 5.394 GPa | 782.3 ksi | ASTM D790 |
| Izod Impact, Notched | 0.340 J/cm | 0.637 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.7 | 3.7 | ASTM D150 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | ASTM D149 |
| Arc Resistance | 119 sec | 119 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 40.0 μm/m-°C | 22.2 μin/in-°F | ASTM D696 |
| Melting Point | 255 °C | 491 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |