- 熔體流動(dòng)速率 [g/10min]: 30.0
- 吸水率 [%]: 0.3
- 缺口沖擊強(qiáng)度: 10.0
- 彎曲模量 [MPa]: 15.5
- 熱變形溫度 [℃]: 225.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.69 g/cc | 1.69 g/cc | ISO 1183 | ||
| Bulk Density | 0.800 g/cc | 0.0289 lb/in3 | ISO 60 | ||
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 50% RH; ISO 62 | ||
| Water Absorption at Saturation | 0.30 % | 0.30 % | ISO 62 | ||
| Viscosity Test | 80 cm3/g | 80 cm3/g | Viscosity number; ISO 1628-5 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 | ||
| 0.0020 cm/cm | 0.0020 in/in | 60x60x2; 270°C / MT 90°C; 600 bar; ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 | ||
| 0.0080 cm/cm | 0.0080 in/in | 60x60x2; 270°C / MT 90°C; 600 bar; ISO 294-4 | |||
| Melt Flow | 30 g/10 min @Load 5.00 kg, Temperature 260 °C | 30 g/10 min @Load 11.0 lb, Temperature 500 °F | ISO 1133-1 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 250 MPa | 36300 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527-1, -2; 5 mm/min | ||
| Elongation at Break | 1.9 % | 1.9 % | ISO 527-1, -2; 5 mm/min | ||
| Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527-1, -2; 1 mm/min | ||
| Flexural Strength | 260 MPa @Strain 2.10 % | 37700 psi @Strain 2.10 % | 2 mm/min; ISO 178-A | ||
| Flexural Modulus | 15.5 GPa | 2250 ksi | 2 mm/min; ISO 178-A | ||
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m2 @Temperature 23.0 °C | <= 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 180-1A | ||
| <= 10.0 kJ/m2 @Temperature -30.0 °C | <= 4.76 ft-lb/in2 @Temperature -22.0 °F | ISO 180-1A | |||
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m2 @Temperature -30.0 °C | 26.2 ft-lb/in2 @Temperature -22.0 °F | ISO 180-1U | ||
| 60.0 kJ/m2 @Temperature 23.0 °C | 28.6 ft-lb/in2 @Temperature 73.4 °F | ISO 180-1U | |||
| Charpy Impact Unnotched | 6.00 J/cm2 @Temperature 23.0 °C | 28.6 ft-lb/in2 @Temperature 73.4 °F | ISO 179-1eU | ||
| 6.50 J/cm2 @Temperature -30.0 °C | 30.9 ft-lb/in2 @Temperature -22.0 °F | ISO 179-1eU | |||
| Charpy Impact, Notched | <= 1.00 J/cm2 @Temperature -30.0 °C | <= 4.76 ft-lb/in2 @Temperature -22.0 °F | ISO 179-1eA | ||
| <= 1.00 J/cm2 @Temperature 23.0 °C | <= 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 179-1eA | |||
| Tensile Creep Modulus, 1 hour | 16500 MPa | 2.39e+6 psi | ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 15000 MPa | 2.18e+6 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 4.2 @Frequency 1.00e+6 Hz | 4.2 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.3 @Frequency 100 Hz | 4.3 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 28.0 kV/mm @Thickness 1.00 mm | 711 kV/in @Thickness 0.0394 in | IEC 60243-1 | ||
| Dissipation Factor | 0.0020 @Frequency 100 Hz | 0.0020 @Frequency 100 Hz | IEC 60250 | ||
| 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 250 V | 250 V | d.a.m.; Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 μm/m-°C @Temperature 23.0 - 55.0 °C | 11.1 μin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1, -2 | ||
| CTE, linear, Transverse to Flow | 80.0 μm/m-°C @Temperature 23.0 - 55.0 °C | 44.4 μin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1, -2 | ||
| Thermal Conductivity | 0.270 W/m-K | 1.87 BTU-in/hr-ft2-°F | ISO 8302 | ||
| Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1, -3 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | IEC 60216-1, Tensile impact strength, 20000 h | ||
| 155 °C | 311 °F | IEC 60216-1, Tensile strength, 20000 h | |||
| 155 °C | 311 °F | IEC 60216-1, Electric strength, 20000 h | |||
| 220 °C | 428 °F | Resistance to heat - ball pressure test; IEC 60695-10-2 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 8.0 MPa | 150 °C | 302 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 210 °C @Load 5.10 kg | 410 °F @Load 11.2 lb | 120°C/hour; ISO 306 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | ||||
| Oxygen Index | 21 % | 21 % | Method A; ISO 4589-2 | ||
| Glow Wire Test | 750 °C @Diameter 2.00 mm | 1380 °F @Diameter 0.0787 in | GWFI; IEC 60695-2-12 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |||
| 270 °C | 518 °F | for test specimens; ISO 294 | |||
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| 90.0 °C | 194 °F | for test specimens; ISO 294 | |||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4 - 8 hour | 4 - 8 hour | |||
| Moisture Content | 0.00 - 0.020 % | 0.00 - 0.020 % | residual; Karl Fischer Test | ||
| Descriptive Properties | |||||
| Electrolytic Corrosion | IEC 60426 | A 1 | |||
| Halving Interval (°C) | 10.2 | IEC 60216-1, Tensile strength | |||
| 10.2 | IEC 60216-1, Electric strength | ||||
| 13.5 | IEC 60216-1, Tensile impact strength | ||||
| ISO Shortname | ISO 7792-1-PBT+PET, GHLMR, 09-160, GF45 | ||||