- 熔體流動速率 [g/10min]: 65.0
- 密度 [g/cm3]: 1.48
- 彎曲強度 [MPa]: 110.0
- 熱變形溫度 [℃]: 214.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in3 | ISO 1183 | ||
| Viscosity Test | 86 cm3/g | 86 cm3/g | Viscosity number | ||
| Melt Flow | 65 g/10 min @Load 2.16 kg, Temperature 275 °C | 65 g/10 min @Load 4.76 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 1.9 % | 1.9 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 7.50 GPa | 1090 ksi | 1mm/min; ISO 527 | ||
| Charpy Impact Unnotched | 2.60 J/cm2 | 12.4 ft-lb/in2 | ISO 179 | ||
| 2.40 J/cm2 @Temperature -30.0 °C | 11.4 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 0.590 J/cm2 | 2.81 ft-lb/in2 | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 223 °C | 433 °F | 10 K/min | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | BK15029 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||