- 密度 [g/cm3]: 1.56
- 彎曲模量 [MPa]: 6.80
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in3 | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527 | ||
| Elongation at Break | 1.5 % | 1.5 % | ISO 527 | ||
| Flexural Modulus | 6.80 GPa | 986 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 1.50 J/cm2 @Temperature 5.00 °C | 7.14 ft-lb/in2 @Temperature 41.0 °F | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 245 °C | 473 °F | ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |||
| Mold Temperature | 100 - 110 °C | 212 - 230 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | 0.20 % | 0.20 % | |||
| Descriptive Properties | |||||
| Color | WT 7792 | ||||
| Commercial Status | North America | ||||