- 密度 [g/cm3]: 1.32
- 缺口沖擊強度: 0.95
- 彎曲強度 [MPa]: 155.0
- 彎曲模量 [MPa]: 8.97
- 硬度: 118.0
- 熱變形溫度 [℃]: 240.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in3 | Melt; ISO 1183 | ||
| 1.55 g/cc | 0.0560 lb/in3 | ISO 1183 | |||
| Viscosity Measurement | 0.55 | 0.55 | Inherent Viscosity | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 118 | 118 | ASTM Test | ||
| Tensile Strength at Break | 155 MPa | 22500 psi | 0.2 in/min; ASTM Test | ||
| 65.0 MPa @Temperature 120 °C | 9430 psi @Temperature 248 °F | ISO Data | |||
| 65.0 MPa @Temperature 120 °C | 9430 psi @Temperature 248 °F | ASTM Test | |||
| 80.0 MPa @Temperature 80.0 °C | 11600 psi @Temperature 176 °F | ASTM Test | |||
| 80.0 MPa @Temperature 80.0 °C | 11600 psi @Temperature 176 °F | ISO Data | |||
| 210 MPa @Temperature -40.0 °C | 30500 psi @Temperature -40.0 °F | ISO Data | |||
| 210 MPa @Temperature -40.0 °C | 30500 psi @Temperature -40.0 °F | ASTM Test | |||
| Tensile Strength, Ultimate | 155 MPa | 22500 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | ||
| 3.5 % | 3.5 % | 5mm/min; ISO 527 | |||
| Tensile Modulus | 10.2 GPa | 1480 ksi | 1mm/min; ISO 527 | ||
| 2.94 GPa @Temperature 120 °C | 426 ksi @Temperature 248 °F | ISO Data | |||
| 4.95 GPa @Temperature 80.0 °C | 718 ksi @Temperature 176 °F | ISO Data | |||
| 10.4 GPa @Temperature -40.0 °C | 1510 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 240 MPa | 34800 psi | ASTM Test | ||
| 85.0 MPa @Temperature 120 °C | 12300 psi @Temperature 248 °F | ASTM Test | |||
| 105 MPa @Temperature 93.0 °C | 15200 psi @Temperature 199 °F | ASTM Test | |||
| 170 MPa @Temperature 65.0 °C | 24700 psi @Temperature 149 °F | ASTM Test | |||
| 275 MPa @Temperature -40.0 °C | 39900 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 8.97 GPa | 1300 ksi | ASTM Test | ||
| 2.83 GPa @Temperature 120 °C | 410 ksi @Temperature 248 °F | ASTM Test | |||
| 3.44 GPa @Temperature 93.0 °C | 499 ksi @Temperature 199 °F | ASTM Test | |||
| 6.13 GPa @Temperature 65.0 °C | 889 ksi @Temperature 149 °F | ASTM Test | |||
| Izod Impact, Notched | 0.950 J/cm @Thickness 3.17 mm | 1.78 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Charpy Impact, Notched | 0.900 J/cm2 | 4.28 ft-lb/in2 | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz | 3.5 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.7 @Frequency 100 Hz | 3.7 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 0.020 @Frequency 100 Hz | 0.020 @Frequency 100 Hz | IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 23.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 12.8 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| CTE, linear, Parallel to Flow | 23.0 μm/m-°C | 12.8 μin/in-°F | ASTM Test | ||
| Specific Heat Capacity | 2.287 J/g-°C | 0.5466 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft2-°F | Melt | ||
| Melting Point | 245 °C | 473 °F | 10 K/min | ||
| 245 °C | 473 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 | ||
| 220 °C | 428 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 115 °C | 239 °F | Injection molding | ||
| Injection Velocity | 115 mm/sec | 4.53 in/sec | Injection molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| UL.UL-C | Yes | ||||