- 密度 [g/cm3]: 1.55
- 缺口沖擊強度: 1.0
- 彎曲強度 [MPa]: 150.0
- 彎曲模量 [MPa]: 8.83
- 硬度: 118.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in3 | ISO 1183 | ||
| Viscosity Measurement | 0.55 | 0.55 | Inherent Viscosity | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 118 | 118 | ASTM Test | ||
| Tensile Strength at Break | 150 MPa | 21800 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 150 MPa | 21800 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |||
| Flexural Strength | 240 MPa | 34800 psi | ASTM Test | ||
| Flexural Modulus | 8.83 GPa | 1280 ksi | ISO Data | ||
| 9.09 GPa | 1320 ksi | ASTM Test | |||
| Izod Impact, Notched | 1.00 J/cm @Thickness 3.17 mm | 1.87 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 9.50 kJ/m2 | 4.52 ft-lb/in2 | ISO Test | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 23.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 12.8 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Melting Point | 245 °C | 473 °F | 10 K/min | ||
| 245 °C | 473 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 115 °C | 239 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | GY6128 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| UL.UL-C | Yes | ||||