- 熔體流動速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.2
- 拉伸強度 [MPa]: 50.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in3 | ISO 1183 | ||
| 1.03 g/cc @Temperature 270 °C | 0.0372 lb/in3 @Temperature 518 °F | Melt | |||
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 260 °C | 12 g/10 min @Load 11.0 lb, Temperature 500 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527-1/-2 | ||
| Elongation at Break | >= 50 % | >= 50 % | Nominal; ISO 527-1/-2 | ||
| Elongation at Yield | 4.5 % | 4.5 % | ISO 527-1/-2 | ||
| Tensile Modulus | 2.10 GPa | 305 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 5.50 J/cm2 | 26.2 ft-lb/in2 | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 70.0 μm/m-°C | 38.9 μin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 70.0 μm/m-°C | 38.9 μin/in-°F | ISO 11359-1/-2 | ||
| Specific Heat Capacity | 1.76 J/g-°C | 0.421 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.165 W/m-K | 1.15 BTU-in/hr-ft2-°F | Melt | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | ||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | IEC 60695-11-10 | |||
| Oxygen Index | 20 % | 20 % | ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 °C | 518 °F | Injection Molding; ISO 294 | ||
| 260 - 280 °C | 500 - 536 °F | ||||
| Mold Temperature | 70.0 °C | 158 °F | Injection Molding; ISO 10724 | ||
| 60.0 - 80.0 °C | 140 - 176 °F | ||||
| Ejection Temperature | 170 °C | 338 °F | |||
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 | ||
| Descriptive Properties | |||||
| Availability | Asia Pacific | ||||
| Europe | |||||
| India | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Eff. thermal diffusivity (m2/s) | 9.08E-08 | ||||
| Feature | Release agent | ||||
| Form | Pellets | ||||
| Process | Injection Molding | ||||