- 缺口沖擊強度: 0.641
- 彎曲模量 [MPa]: 8.998
- 熱變形溫度 [℃]: 227.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.175 mm | 0.0020 in/in @Thickness 0.1250 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 140 MPa | 20300 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 205 MPa | 29700 psi | ASTM D790 |
| Flexural Modulus | 8.998 GPa | 1305 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.41 J/cm | 12.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 227 °C | 441 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 90.0 - 110 °C | 194 - 230 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |