- 密度 [g/cm3]: 1.67
- 缺口沖擊強度: 1.01
- 彎曲強度 [MPa]: 127.0
- 彎曲模量 [MPa]: 16.2
- 硬度: 120.0
- 熱變形溫度 [℃]: 223.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in3 | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 127 MPa | 18400 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 208 MPa | 30200 psi | ASTM D790 |
| Flexural Modulus | 16.2 GPa | 2350 ksi | ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 258 - 268 °C | 496 - 514 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 296 - 304 °C | 565 - 579 °F | Approximate middle barrel temperature range |