- 密度 [g/cm3]: 1.31
- 缺口沖擊強度: 1.17
- 彎曲強度 [MPa]: 85.0
- 彎曲模量 [MPa]: 5.70
- 硬度: 106.0
- 熱變形溫度 [℃]: 141.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in3 | |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ASTM D638 |
| Elongation at Break | 8.5 % | 8.5 % | ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 5.70 GPa | 827 ksi | ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.66 J/cm | 10.6 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
| Glass Transition Temp, Tg | 145 - 150 °C | 293 - 302 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 254 - 271 °C | 489 - 520 °F | Approximate middle barrel temperature range |