- 密度 [g/cm3]: 1.74
- 缺口沖擊強度: 0.53
- 彎曲強度 [MPa]: 108.0
- 彎曲模量 [MPa]: 9.50
- 硬度: 116.0
- 熱變形溫度 [℃]: 94.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in3 | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength, Ultimate | 108 MPa | 15700 psi | ASTM D638 |
| Elongation at Break | 3.7 % | 3.7 % | ASTM D638 |
| Flexural Strength | 157 MPa | 22800 psi | ASTM D790 |
| Flexural Modulus | 9.50 GPa | 1380 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.96 J/cm | 9.29 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 258 - 268 °C | 496 - 514 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C | 201 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C | 174 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 296 - 304 °C | 565 - 579 °F | Approximate middle barrel temperature range |