- 密度 [g/cm3]: 1.67
- 缺口沖擊強度: 0.9
- 彎曲強度 [MPa]: 135.0
- 彎曲模量 [MPa]: 9.93
- 硬度: 118.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 118 | 118 | ASTM Test | ||
| Tensile Strength at Break | 135 MPa | 19600 psi | 0.2 in/min; ASTM Test | ||
| 60.0 MPa @Temperature 120 °C | 8700 psi @Temperature 248 °F | ISO Data | |||
| 60.0 MPa @Temperature 120 °C | 8700 psi @Temperature 248 °F | ASTM Test | |||
| 82.0 MPa @Temperature 80.0 °C | 11900 psi @Temperature 176 °F | ASTM Test | |||
| 82.0 MPa @Temperature 80.0 °C | 11900 psi @Temperature 176 °F | ISO Data | |||
| 170 MPa @Temperature -40.0 °C | 24700 psi @Temperature -40.0 °F | ASTM Test | |||
| 170 MPa @Temperature -40.0 °C | 24700 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Ultimate | 135 MPa | 19600 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.0 % | 2.0 % | 5mm/min; ISO 527 | ||
| 2.0 % | 2.0 % | 0.2 in/min; ASTM Test | |||
| 2.0 % @Temperature -40.0 °C | 2.0 % @Temperature -40.0 °F | ASTM Test | |||
| 2.0 % @Temperature -40.0 °C | 2.0 % @Temperature -40.0 °F | ISO Data | |||
| 4.1 % @Temperature 80.0 °C | 4.1 % @Temperature 176 °F | ASTM Test | |||
| 4.1 % @Temperature 80.0 °C | 4.1 % @Temperature 176 °F | ISO Data | |||
| 5.7 % @Temperature 120 °C | 5.7 % @Temperature 248 °F | ASTM Test | |||
| 5.7 % @Temperature 120 °C | 5.7 % @Temperature 248 °F | ISO Data | |||
| Flexural Strength | 215 MPa | 31200 psi | ASTM Test | ||
| Flexural Modulus | 9.93 GPa | 1440 ksi | ASTM Test | ||
| Izod Impact, Notched | 0.900 J/cm @Thickness 3.17 mm | 1.69 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.7 @Frequency 100 Hz | 3.7 @Frequency 100 Hz | IEC 60250 | ||
| 3.9 @Frequency 1.00e+6 Hz | 3.9 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 0.020 @Frequency 100 Hz | 0.020 @Frequency 100 Hz | IEC 60250 | |||
| Comparative Tracking Index | 260 V | 260 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 250 °C | 482 °F | 10 K/min | ||
| 255 °C | 491 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 223 °C | 433 °F | ASTM Test | ||
| Flammability, UL94 | V-0 @Thickness 0.300 mm | V-0 @Thickness 0.0118 in | |||
| Descriptive Properties | |||||
| Color | BK-112 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| UL.UL-C | Yes | ||||