- 密度 [g/cm3]: 1.55
- 缺口沖擊強度: 0.95
- 彎曲強度 [MPa]: 145.0
- 彎曲模量 [MPa]: 8.25
- 硬度: 118.0
- 熱變形溫度 [℃]: 235.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in3 | ISO 1183 | ||
| Viscosity Measurement | 0.55 | 0.55 | Inherent Viscosity | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 118 | 118 | ASTM Test | ||
| Tensile Strength at Break | 145 MPa | 21000 psi | 0.2 in/min; ASTM Test | ||
| 54.0 MPa @Temperature 120 °C | 7830 psi @Temperature 248 °F | ISO Data | |||
| 211 MPa @Temperature -40.0 °C | 30600 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Ultimate | 145 MPa | 21000 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |||
| 2.3 % @Temperature -40.0 °C | 2.3 % @Temperature -40.0 °F | ISO Data | |||
| 4.0 % @Temperature 120 °C | 4.0 % @Temperature 248 °F | ISO Data | |||
| Tensile Modulus | 10.2 GPa | 1480 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 230 MPa | 33400 psi | ASTM Test | ||
| Flexural Modulus | 8.25 GPa | 1200 ksi | ISO Data | ||
| 8.76 GPa | 1270 ksi | ASTM Test | |||
| Izod Impact, Notched | 0.950 J/cm @Thickness 3.17 mm | 1.78 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 9.50 kJ/m2 | 4.52 ft-lb/in2 | ISO Test | ||
| 8.50 kJ/m2 @Temperature -40.0 °C | 4.04 ft-lb/in2 @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact, Notched | 0.900 J/cm2 | 4.28 ft-lb/in2 | ISO 179 | ||
| 0.850 J/cm2 @Temperature -30.0 °C | 4.05 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 23.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 12.8 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Melting Point | 245 °C | 473 °F | 10 K/min | ||
| 245 °C | 473 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | ASTM Test | ||
| 240 °C | 464 °F | ISO 75 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 | ||
| 215 °C | 419 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 115 °C | 239 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK-112 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| UL.UL-C | Yes | ||||