- 缺口沖擊強(qiáng)度: 1.18
- 彎曲模量 [MPa]: 4.413
- 硬度: 113.0
- 熱變形溫度 [℃]: 155.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.050 % | 0.050 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.0070 - 0.011 cm/cm | 0.0070 - 0.011 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 113 | 113 | ASTM D785 |
| Tensile Strength | 88.0 MPa | 12800 psi | ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | ASTM D638 |
| Flexural Strength | 147 MPa | 21300 psi | ASTM D790 |
| Flexural Modulus | 4.413 GPa | 640.1 ksi | ASTM D790 |
| Izod Impact, Notched | 1.18 J/cm | 2.21 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.6 | 3.6 | ASTM D150 |
| Dielectric Strength | 26.0 kV/mm | 660 kV/in | ASTM D149 |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.0 μm/m-°C | 27.8 μin/in-°F | ASTM D696 |
| Melting Point | 224 °C | 435 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |