- 熔體流動(dòng)速率 [g/10min]: 40.0
- 吸水率 [%]: 0.12
- 缺口沖擊強(qiáng)度: 7.0
- 彎曲模量 [MPa]: 2.20
- 硬度: 118.0
- 熱變形溫度 [℃]: 107.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.21 g/cc @Temperature 23.0 °C | 1.21 g/cc @Temperature 73.4 °F | ASTM D792 | ||
| Water Absorption | 0.12 % @Temperature 23.0 °C, Time 86400 sec | 0.12 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0080 - 0.010 cm/cm @Temperature 23.0 °C | 0.0080 - 0.010 in/in @Temperature 73.4 °F | ASTM D955 | ||
| Melt Flow | 40 g/10 min @Load 5.00 kg, Temperature 260 °C | 40 g/10 min @Load 11.0 lb, Temperature 500 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 118 | 118 | ASTM D785 | ||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50mm/min; ASTM D638 | ||
| Elongation at Break | >= 90 % | >= 90 % | 50mm/min; ASTM D638 | ||
| Flexural Strength | 80.0 MPa | 11600 psi | 2mm/min; ASTM D790 | ||
| Flexural Modulus | 2.20 GPa | 319 ksi | 2mm/min; ASTM D790 | ||
| Izod Impact, Notched | >= 7.00 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | >= 13.1 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 | ||
| Izod Impact, Unnotched | 4.50 J/cm @Thickness 3.20 mm, Temperature -40.0 °C | 8.43 ft-lb/in @Thickness 0.126 in, Temperature -40.0 °F | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 | ||
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | 1.6mm; ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C @Thickness 6.40 mm | 225 °F @Thickness 0.252 in | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C @Thickness 6.40 mm | 208 °F @Thickness 0.252 in | ASTM D648 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 250 °C | <= 482 °F | |||
| Rear Barrel Temperature | 200 - 220 °C | 392 - 428 °F | Start Point: 215°C | ||
| Middle Barrel Temperature | 200 - 225 °C | 392 - 437 °F | Start Point: 215°C | ||
| Front Barrel Temperature | 210 - 230 °C | 410 - 446 °F | Start Point: 220°C | ||
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Start Point: 220°C | ||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Start Point: 70°C | ||
| Drying Temperature | 80.0 - 85.0 °C @Time 10800 - 14400 sec | 176 - 185 °F @Time 3.00 - 4.00 hour | Pre-dry | ||
| Back Pressure | 0.000 - 10.0 MPa | 0.000 - 1450 psi | |||
| Descriptive Properties | |||||
| Injection Speed | 50-80% | ||||