- 缺口沖擊強度: 0.49
- 彎曲模量 [MPa]: 2.452
- 硬度: 118.0
- 熱變形溫度 [℃]: 166.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.070 % | 0.070 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.018 - 0.023 cm/cm | 0.018 - 0.023 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength | 57.0 MPa | 8270 psi | ASTM D638 |
| Elongation at Break | 75 % | 75 % | ASTM D638 |
| Flexural Strength | 93.0 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 2.452 GPa | 355.6 ksi | ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.1 | 3.1 | ASTM D150 |
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | ASTM D149 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 80.0 μm/m-°C | 44.4 μin/in-°F | ASTM D696 |
| Melting Point | 224 °C | 435 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 331 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |