- 吸水率 [%]: 0.07
- 缺口沖擊強度: 0.8
- 彎曲模量 [MPa]: 9.00
- 硬度: 120.0
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.61 g/cc @Temperature 23.0 °C | 1.61 g/cc @Temperature 73.4 °F | ASTM D792 | ||
| Water Absorption | 0.070 % @Temperature 23.0 °C, Time 86400 sec | 0.070 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0030 - 0.0090 cm/cm @Temperature 23.0 °C | 0.0030 - 0.0090 in/in @Temperature 73.4 °F | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 120 | 120 | ASTM D785 | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | 10mm/min; ASTM D638 | ||
| Elongation at Break | 2.6 % | 2.6 % | 10mm/min; ASTM D638 | ||
| Flexural Strength | 190 MPa | 27600 psi | 2mm/min; ASTM D790 | ||
| Flexural Modulus | 9.00 GPa | 1310 ksi | 2mm/min; ASTM D790 | ||
| Izod Impact, Notched | 0.800 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 1.50 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C @Thickness 6.40 mm | 428 °F @Thickness 0.252 in | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C @Thickness 6.40 mm | 410 °F @Thickness 0.252 in | ASTM D648 | ||
| Flammability, UL94 | V-0 @Thickness 0.700 mm | V-0 @Thickness 0.0276 in | |||
| V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 265 °C | <= 509 °F | |||
| Rear Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Start Point: 235°C | ||
| Middle Barrel Temperature | 235 - 255 °C | 455 - 491 °F | Start Point: 245°C | ||
| Front Barrel Temperature | 240 - 265 °C | 464 - 509 °F | Start Point: 255°C | ||
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | Start Point: 250°C | ||
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | Start Point: 60°C | ||
| Drying Temperature | 120 - 140 °C @Time 14400 - 21600 sec | 248 - 284 °F @Time 4.00 - 6.00 hour | Pre-dry | ||
| Descriptive Properties | |||||
| Glass Fiber Content (%) | 30 | ||||
| Injection Speed | Moderate to High | ||||