- 熔體流動速率 [g/10min]: 13.0
- 密度 [g/cm3]: 1.42
- 拉伸強度 [MPa]: 55.0
- 熱變形溫度 [℃]: 150.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in3 | |
| Water Absorption | 0.00 % | 0.00 % | |
| Moisture Absorption at Equilibrium | <= 0.50 % | <= 0.50 % | Humidity Absorption |
| Melt Flow | 13 g/10 min | 13 g/10 min | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 7.0 % | 7.0 % | |
| Modulus of Elasticity | 2.20 GPa | 319 ksi | |
| Charpy Impact Unnotched | 9.00 J/cm2 | 42.8 ft-lb/in2 | |
| 6.50 J/cm2 @Temperature -30.0 °C | 30.9 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 0.300 J/cm2 | 1.43 ft-lb/in2 | |
| 0.300 J/cm2 @Temperature -30.0 °C | 1.43 ft-lb/in2 @Temperature -22.0 °F | ||
| Tensile Impact Strength | 50.0 kJ/m2 | 23.8 ft-lb/in2 | |
| Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | |
| Tensile Creep Modulus, 1000 hours | 1100 MPa | 160000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 3.0 @Frequency 100 Hz | 3.0 @Frequency 100 Hz | |
| 3.0 @Frequency 1e+6 Hz | 3.0 @Frequency 1e+6 Hz | ||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | |
| Dissipation Factor | 0.0060 @Frequency 100 Hz | 0.0060 @Frequency 100 Hz | |
| 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | ||
| Comparative Tracking Index | 175 V | 175 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 100 μm/m-°C @Temperature 20.0 °C | 55.6 μin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 100 μm/m-°C @Temperature 20.0 °C | 55.6 μin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| Vicat Softening Point | 155 °C | 311 °F | 50°C/hr/50 N |
| UL RTI, Electrical | 130 °C | 266 °F | |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | |
| UL RTI, Mechanical without Impact | 140 °C | 284 °F | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |
| V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | ||