- 熔體流動速率 [g/10min]: 19.0
- 缺口沖擊強度: 0.588
- 彎曲強度 [MPa]: 98.1
- 彎曲模量 [MPa]: 5.88
- 熱變形溫度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc @Temperature 23.0 °C | 1.51 g/cc @Temperature 73.4 °F | ASTM D792 |
| Filler Content | 15 % | 15 % | |
| Linear Mold Shrinkage | 0.0050 - 0.012 cm/cm | 0.0050 - 0.012 in/in | ASTM D955 |
| Melt Flow | 19 g/10 min @Load 2.16 kg, Temperature 250 °C | 19 g/10 min @Load 4.76 lb, Temperature 482 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 98.1 MPa | 14200 psi | 5mm/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | 5mm/min; ASTM D638 |
| Flexural Strength | 152 MPa | 22000 psi | 2.8mm/min; ASTM D790 |
| Flexural Modulus | 5.88 GPa | 853 ksi | 2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.588 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 1.10 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 230 - 265 °C | 446 - 509 °F | Cylinder Temperature |
| Mold Temperature | 50.0 - 100 °C | 122 - 212 °F | |
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour | |