- 熔體流動速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.66
- 拉伸強度 [MPa]: 120.0
- 熱變形溫度 [℃]: 190.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in3 | |
| Water Absorption | 0.00 % | 0.00 % | |
| Moisture Absorption at Equilibrium | <= 0.50 % | <= 0.50 % | Humidity Absorption |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 120 MPa | 17400 psi | |
| Elongation at Break | 5.0 % | 5.0 % | |
| Elongation at Yield | 3.0 % | 3.0 % | |
| Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
| Charpy Impact Unnotched | 6.00 J/cm2 | 28.6 ft-lb/in2 | |
| 6.00 J/cm2 @Temperature -30.0 °C | 28.6 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.40 J/cm2 | 6.66 ft-lb/in2 | |
| 1.00 J/cm2 @Temperature -30.0 °C | 4.76 ft-lb/in2 @Temperature -22.0 °F | ||
| Tensile Impact Strength | 8.00 kJ/m2 | 3.81 ft-lb/in2 | |
| Tensile Creep Modulus, 1 hour | 6800 MPa | 986000 psi | |
| Tensile Creep Modulus, 1000 hours | 5100 MPa | 740000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz | 3.0 @Frequency 1e+6 Hz | |
| 4.0 @Frequency 100 Hz | 4.0 @Frequency 100 Hz | ||
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | |
| Dissipation Factor | 0.010 @Frequency 100 Hz | 0.010 @Frequency 100 Hz | |
| 0.018 @Frequency 1e+6 Hz | 0.018 @Frequency 1e+6 Hz | ||
| Comparative Tracking Index | 225 V | 225 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | <= 50.0 μm/m-°C @Temperature 20.0 °C | <= 27.8 μin/in-°F @Temperature 68.0 °F | |
| CTE, linear, Transverse to Flow | <= 50.0 μm/m-°C @Temperature 20.0 °C | <= 27.8 μin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | |
| Vicat Softening Point | 165 °C | 329 °F | 50°C/hr/50 N |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |
| V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | ||