- 熔體流動(dòng)速率 [g/10min]: 25.0
- 密度 [g/cm3]: 1.56
- 拉伸強(qiáng)度 [MPa]: 60.0
- 熱變形溫度 [℃]: 170.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in3 | |
| Water Absorption | 0.00 % | 0.00 % | |
| Moisture Absorption at Equilibrium | <= 0.50 % | <= 0.50 % | Humidity Absorption |
| Melt Flow | 25 g/10 min | 25 g/10 min | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | |
| Elongation at Break | 10 % | 10 % | |
| Elongation at Yield | 7.0 % | 7.0 % | |
| Modulus of Elasticity | 3.30 GPa | 479 ksi | |
| Charpy Impact Unnotched | 15.0 J/cm2 | 71.4 ft-lb/in2 | |
| 12.0 J/cm2 @Temperature -30.0 °C | 57.1 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 0.500 J/cm2 | 2.38 ft-lb/in2 | |
| 0.400 J/cm2 @Temperature -30.0 °C | 1.90 ft-lb/in2 @Temperature -22.0 °F | ||
| Tensile Impact Strength | 55.0 kJ/m2 | 26.2 ft-lb/in2 | |
| Tensile Creep Modulus, 1 hour | 3300 MPa | 479000 psi | |
| Tensile Creep Modulus, 1000 hours | 1200 MPa | 174000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 4.0 @Frequency 100 Hz | 4.0 @Frequency 100 Hz | |
| 4.0 @Frequency 1e+6 Hz | 4.0 @Frequency 1e+6 Hz | ||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | |
| Dissipation Factor | 0.0065 @Frequency 100 Hz | 0.0065 @Frequency 100 Hz | |
| 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | ||
| Comparative Tracking Index | 425 V | 425 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 100 μm/m-°C @Temperature 20.0 °C | 55.6 μin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 100 μm/m-°C @Temperature 20.0 °C | 55.6 μin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | |
| Vicat Softening Point | 190 °C | 374 °F | 50°C/hr/50 N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |