- 熔體流動速率 [g/10min]: 34.0
- 缺口沖擊強度: 2.14
- 拉伸強度 [MPa]: 57.2
- 斷裂伸長率 [%]: 75.8
- 彎曲模量 [MPa]: 2.41
- 熱變形溫度 [℃]: 103.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0090 cm/cm | 0.0060 - 0.0090 in/in | ASTM D955 |
| Melt Flow | 34 g/10 min @Load 3.80 kg, Temperature 260 °C | 34 g/10 min @Load 8.38 lb, Temperature 500 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 57.2 MPa | 8300 psi | ASTM D638 |
| Flexural Yield Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm @Thickness 3.17 mm, Temperature -40.0 °C | 4.00 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F | ASTM D256 |
| 6.41 J/cm @Thickness 3.17 mm, Temperature 22.8 °C | 12.0 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.7 °C | 197 °F | Unannealed; ASTM D648 |