- 缺口沖擊強度: 0.481
- 彎曲模量 [MPa]: 4.69
- 熱變形溫度 [℃]: 188.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 cm/cm @Thickness 3.175 mm | 0.0080 in/in @Thickness 0.1250 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 79.3 MPa | 11500 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 121 MPa | 17500 psi | ASTM D790 |
| Flexural Modulus | 4.69 GPa | 680 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.74 J/cm | 7.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 225 °C | 437 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 188 °C | 370 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| Mold Temperature | 30.0 - 65.6 °C | 86.0 - 150 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |