- 缺口沖擊強(qiáng)度: 0.481
- 彎曲模量 [MPa]: 4.48
- 熱變形溫度 [℃]: 182.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.015 cm/cm @Thickness 3.175 mm | 0.015 in/in @Thickness 0.1250 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 49.6 MPa | 7200 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 89.6 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 4.48 GPa | 650 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.94 J/cm | 5.50 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 225 °C | 437 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| Mold Temperature | 30.0 - 65.6 °C | 86.0 - 150 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |