- 缺口沖擊強(qiáng)度: 0.427
- 彎曲模量 [MPa]: 3.45
- 熱變形溫度 [℃]: 177.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
| Elongation at Break | 3.2 % | 3.2 % | ASTM D638 |
| Flexural Strength | 86.2 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm | 0.800 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 225 °C | 437 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| Mold Temperature | 30.0 - 65.6 °C | 86.0 - 150 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |