- 密度 [g/cm3]: 1.59
- 彎曲強度 [MPa]: 58.0
- 彎曲模量 [MPa]: 4.00
- 硬度: 110.0
- 熱變形溫度 [℃]: 110.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in3 | |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Ultimate | 58.0 MPa | 8410 psi | ASTM D638 |
| Elongation at Break | 5.4 % | 5.4 % | ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 4.00 GPa | 580 ksi | ASTM D790 |
| Izod Impact, Unnotched | 3.42 J/cm | 6.41 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 210 - 225 °C | 410 - 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 235 - 249 °C | 455 - 480 °F | Approximate middle barrel temperature range |