- 密度 [g/cm3]: 0.075
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0750 g/cc | 0.00271 lb/in3 | DIN 53420, ISO 845, ASTM D 1622 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 1.50 MPa | 218 psi | DIN 53455, ISO 527-2, ASTM D 638 |
| Elongation at Break | 9.0 % | 9.0 % | DIN 53455, ISO 527-2, ASTM D 638 |
| Modulus of Elasticity | 0.0650 GPa | 9.43 ksi | ISO 527-2, ASTM D 638 |
| Compressive Strength | 0.800 MPa | 116 psi | DIN 53421, ISO 844, ASTM D 1621 |
| Poissons Ratio | 0.25 | 0.25 | Calculated |
| Shear Modulus | 0.0260 GPa | 3.77 ksi | DIN 53294, ASTM C 273 |
| Shear Strength | 0.700 MPa | 102 psi | DIN 53294, ASTM C 273 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 180 °C | 356 °F | Heat Distortion Resistance; DIN 53424 |