- 密度 [g/cm3]: 0.2052
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.2052 g/cc | 0.007413 lb/in3 | DIN 53420, ISO 845, ASTM D 1622 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 6.80 MPa | 986 psi | DIN 53455, ISO 527-2, ASTM D 638 |
| Elongation at Break | 3.5 % | 3.5 % | DIN 53455, ISO 527-2, ASTM D 638 |
| Modulus of Elasticity | 0.350 GPa | 50.8 ksi | ISO 527-2, ASTM D 638 |
| Flexural Strength | 12.0 MPa | 1740 psi | DIN 53423, ISO 1209, ASTM D 790 |
| Compressive Strength | 9.00 MPa | 1310 psi | DIN 53421, ISO 844, ASTM D 1621 |
| Shear Modulus | 0.150 GPa | 21.8 ksi | DIN 53294, ASTM C 273 |
| Shear Strength | 5.00 MPa | 725 psi | DIN 53294, ASTM C 273 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 200 °C | 392 °F | Heat Distortion Resistance; DIN 53424 |